PolyOne Lubri-Tech™ AT-15GM/15T Acetal-Copolymer, Glass Filled, PTFE Lubricated (discontinued **)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ AT-15GM/15T Acetal-Copolymer, Glass Filled, PTFE Lubricated
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Milled Glass Fiber ReinforcedPTFE LubricatedUL 94 HBPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.60 g/cc | 1.60 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 41.4 MPa | 6000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 3.10 GPa | 450 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Izod Impact, Notched | 0.427 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
0.800 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 188 - 210 °C | 370 - 410 °F | Molding |
| Mold Temperature | 48.9 - 98.9 °C | 120 - 210 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Nilit Nilamid A G5 FR PH2 25% Glass Fiber Reinforced, Flame Retardant PA66 (with Red Phosphorous)
- PolyOne Lubri-Tech™ ATH-000/02T Homopolymer - 2% PTFE (discontinued **)
- Lubriplate SYNAC 68 Diester-Based Synthetic Air Compressor Fluid
- Techmer ES HiFill® ABS 1067
- A. Schulman POLYFORT™ FPP 1236 Glass Filled Chemically Coupled Homopolymer Polypropylene
- Dow Corning AMS-C30 Cosmetic Wax
- DuPont™ Nomex® E56 Paper, 10 mil Nominal Thickness
- ExxonMobil 220 Mobilgear SHC Series
- Axiall 3121 Rigid PVC, Extrusion
Copyright © lookpolymers.com All Rights Reserved