- Hexcel® HexPly® M26/M26T 120°C (250°F) Curing Epoxy Matrix, M26/45%/G1070 Carbon Fabric
Hexcel® HexPly® M26/M26T 120°C (250°F) Curing Epoxy Matrix, M26/45%/G1070 Carbon Fabric
| Category | Polymer , Thermoset , Carbon Fiber/Thermoset Composite , Epoxy , Epoxy/Carbon Fiber Composite |
| Manufacturer | Hexcel |
| Trade Name | HexPly® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hexcel® HexPly® M26/M26T 120°C (250°F) Curing Epoxy Matrix, M26/45%/G1070 Carbon Fabric.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
6K T300J 370 gsmInformation provided by HexCel
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 780 MPa @Temperature 80.0 °C |
113000 psi @Temperature 176 °F |
Warp TS |
| 790 MPa @Temperature 23.0 °C |
115000 psi @Temperature 73.4 °F |
||
| Flexural Yield Strength | 580 MPa @Temperature 80.0 °C |
84100 psi @Temperature 176 °F |
Warp |
| 900 MPa @Temperature 23.0 °C |
131000 psi @Temperature 73.4 °F |
||
| Flexural Modulus | 51.0 GPa @Temperature 80.0 °C |
7400 ksi @Temperature 176 °F |
Warp |
| 58.0 GPa @Temperature 23.0 °C |
8410 ksi @Temperature 73.4 °F |
||
| Compressive Yield Strength | 700 MPa | 102000 psi | Warp, RT |
| Compressive Modulus | 62.0 GPa | 8990 ksi | Warp, RT |
| Shear Strength | 71.0 MPa | 10300 psi | Warp ILSS, RT |
| 45.0 MPa @Temperature 80.0 °C |
6530 psi @Temperature 176 °F |
Warp ILSS | |
| 92.0 MPa @Temperature -55.0 °C |
13300 psi @Temperature -67.0 °F |
Warp ILSS |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Shelf Life | 12.0 Month @Temperature -18.0 °C |
12.0 Month @Temperature -0.400 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Fiber Volume (%) | 55 |
Users viewing this material also viewed the following:
- Premix Thermoplastics PREFLEX E12.5 Polyphenylene Ether (PPO/PPE)
- Proto3000 Objet DurusWhite FullCure430 Polypropylene-like Prototyping Polymer
- PolyOne Elastamax™ XL 1088-10 Styrene Butadiene Block Copolymer (SBC) with Mineral Filler (discontinued **)&l
- LyondellBasell Alathon® L5332CP High Density Polyethylene, Blow Molding Grade
- Fiberfil® FV-30 Nylon 6, 30% Glass Reinforced, Heat Stabilized
- LG Chemical Lupox® SG5500 PBT+PET+GF50%
- Johnson Matthey LM 15 Soft Solder/Flux
- ChevronTexaco ECO® SAE 40 Heavy Duty Motor Oil
- 3M FP032302W White Metallized Polypropylene Label Products
- Albis Plastics Cellulose Acetate Butyrate B9024 (UVI, Odor Mask Added), 20% Plasticizer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved