Seals Eastern 7352D Nano-PTFE Filled Fluoroelastomer
| Category | Polymer , Thermoset , Filled/Reinforced Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Seals Eastern, Inc |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Seals Eastern 7352D Nano-PTFE Filled Fluoroelastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nano-PTFE filled fluoroelastomer for low wear in hot dynamic applicationsInformation provided by Seals Eastern.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 80 | >= 80 | ASTM D2240 |
| 90 | 90 | Average; ASTM D2240 | |
| Tensile Strength | >= 17.2 MPa | >= 2500 psi | ASTM D412 Method A |
| 18.6 MPa | 2700 psi | Average; ASTM D412 Method A | |
| Tensile Stress | 2.59 MPa @Strain 25.0 % |
375 psi @Strain 25.0 % |
Average; ASTM D412 Method A |
| >= 3.31 MPa @Strain 50.0 % |
>= 480 psi @Strain 50.0 % |
ASTM D412 Method A | |
| 3.34 MPa @Strain 50.0 % |
485 psi @Strain 50.0 % |
Average; ASTM D412 Method A | |
| >= 4.83 MPa @Strain 100 % |
>= 700 psi @Strain 100 % |
ASTM D412 Method A | |
| 4.90 MPa @Strain 100 % |
710 psi @Strain 100 % |
Average; ASTM D412 Method A | |
| Elongation at Break | >= 290 % | >= 290 % | ASTM D412 Method A |
| 320 % | 320 % | Average; ASTM D412 Method A | |
| Modulus of Elasticity | 0.01991 GPa | 2.887 ksi | Calculated; ASTM D412 Method A |
| Shear Modulus | 0.00663 GPa | 0.962 ksi | Calculated; ASTM D412 Method A |
| Secant Modulus | 0.01862 GPa | 2.701 ksi | ASTM D412 Method A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 93.3 °C | 200 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Shelf Life | 240 Month | 240 Month |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Strain Energy/ Unit Volume at 20% Elongation (psi) | 51 | ASTM D412 Method A |
Users viewing this material also viewed the following:
- Resin Technology Group Fusion 900 Odorless, Non-Frosting Fusion Cyanoacrylate
- Kinlead HSD13 Normal Grade Heat Sealable Film (thickness: 18 µm)
- Shandong Rike Chemical RIKEâ„¢ RK-870G MBS Impact Modifier for PVC Transparent Product
- Eurotec® Tecodur® PB70 GR30 NL XA60 PBT, 30% glass fiber reinforced, flame retardant - halogen & red phosphorus, heat stabilized, natural
- CMW® ELKONITE® TC20 Tungsten Carbide Copper material
- BASF Ultramid® 8270 HS PA6 (Dry)
- 3M 8412 Polyester Film Tape
- 3M FM01961K MC Polyester Label Product
- Less Common Metals LaNi5 Cast Hydrogen Storage
- A. Schulman POLYBATCH™ White L8350 HSF Concentrate Based In High-Flow LLDPE