Westlake EF444 4.7% Ethylene Vinyl Acetate Copolymer (discontinued **)

Category	Polymer , Thermoplastic , Ethylene Vinyl Acetate
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Westlake EF444 4.7% Ethylene Vinyl Acetate Copolymer (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Excellent haze and gloss, excellent impact strength and very good sealability.Application/UsesHigh clarity packagingHigh impactFDA: This material complies with FDA regulations in 21 CFR, section 177.1350. Kosher Compliant.All information provided by Westlake Chemical

Physical Properties	Metric	English	Comments
Density	0.929 g/cc	0.0336 lb/in³	ASTM D1505
Vinyl Acetate Content	4.7 %	4.7 %
Thickness	31.8 microns	1.25 mil
Melt Flow	1.25 g/10 min	1.25 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	300 %	300 %	ASTM D882
Film Elongation at Break, TD	600 %	600 %	ASTM D882
Dart Drop	9.84 g/micron	250 g/mil	ASTM D1709
Film Tensile Strength at Break, MD	27.6 MPa	4000 psi	ASTM D882
Film Tensile Strength at Break, TD	21.4 MPa	3100 psi	ASTM D882
1% Secant Modulus, MD	145 MPa	21000 psi	ASTM D882
1% Secant Modulus, TD	179 MPa	26000 psi	ASTM D882

Optical Properties	Metric	English	Comments
Haze	7.0 %	7.0 %	ASTM D1003
Gloss	63 %	63 %	at 45º; ASTM D2457

Processing Properties	Metric	English	Comments
Melt Temperature	182 - 199 °C	360 - 390 °F	with BUR of 1.5:1 or higher
Blow-up Ratio (BUR)	2.5	2.5

Descriptive Properties	Value	Comments
Process	Film
Region	US & Canada	Bamberger Polymers Distribution