- PlastiComp Complet® LGF50 - PA66 MT Nylon 66, 50% Long Glass Fiber Reinforced, Impact Modified
PlastiComp Complet® LGF50 - PA66 MT Nylon 66, 50% Long Glass Fiber Reinforced, Impact Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled , Nylon 66, Glass Reinforced, Impact Grade |
| Manufacturer | PlastiComp |
| Trade Name | Complēt® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PlastiComp Complet® LGF50 - PA66 MT Nylon 66, 50% Long Glass Fiber Reinforced, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Complēt® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Nylon 6 with 50% long glass fiber reinforcementImpact modifiedInformation provided by PlastiComp, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.60 g/cc | 1.60 g/cc | ASTM D-792 |
| Filler Content | 50 % | 50 % | Long Glass Fiber |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 221 MPa | 32100 psi | ASTM D-638 |
| Elongation at Break | 2.0 - 3.0 % | 2.0 - 3.0 % | ASTM D-638 |
| Tensile Modulus | 15.172 GPa | 2200.5 ksi | ASTM D-638 |
| Flexural Strength | 360 MPa | 52200 psi | ASTM D-790 |
| Flexural Modulus | 11.724 GPa | 1700.4 ksi | ASTM D-790 |
| Izod Impact, Notched | 6.51 J/cm | 12.2 ft-lb/in | ASTM D-256 |
| Izod Impact, Unnotched | 18.16 J/cm | 34.02 ft-lb/in | ASTM D-4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D-648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 282 - 299 °C | 540 - 570 °F | |
| Middle Barrel Temperature | 288 - 304 °C | 550 - 580 °F | |
| Front Barrel Temperature | 293 - 310 °C | 560 - 590 °F | |
| Nozzle Temperature | 288 - 304 °C | 550 - 580 °F | |
| Melt Temperature | 293 - 310 °C | 560 - 590 °F | |
| Mold Temperature | 93.3 °C | 200 °F | |
| Injection Velocity | 50.8 - 76.2 mm/sec | 2.00 - 3.00 in/sec | |
| Drying Temperature | 85.0 °C @Time 14400 sec |
185 °F @Time 4.00 hour |
|
| Moisture Content | <= 0.18 % | <= 0.18 % | |
| Back Pressure | 0.172 - 0.345 MPa | 25.0 - 50.0 psi | |
| Cushion | 0.635 cm | 0.250 in | |
| Screw Speed | 30 - 50 rpm | 30 - 50 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Pressure | Medium to maximum |
Users viewing this material also viewed the following:
- S&E Specialty Polymers GF-91-102-2 PVC
- Polymer Resources PC/ABS-G10 General Purpose PC/ABS Alloy, 10% Glass Filled
- Chevron Phillips 4610 LDPE High Clarity, Bakery Packaging Film Resin (discontinued **)
- Lehmann & Voss LUVOCOM® 1-8070 VP Polyamide 66, with carbon fiber, lubricant modified, heat stabilized
- Gwent Electronic Materials C1991025D2 Gold Ink
- Techmer ES HiFill® PA6/6 GB30 L 30% Glass Bead Filler
- SABIC Innovative Plastics NORYL PPX PPX7115 PPE+PP (Asia Pacific)
- Aclo Accutech Polypropylene Copolymer CP0437G25M5CL Glass/Mineral Reinforced Coupled
- PolyOne Geon™ Vinyl Wire & Cable WC9000L Polyvinyl Chloride, Flexible (PVC, Flexible)
Copyright © lookpolymers.com All Rights Reserved