PolyOne LubriOne™ AT-000/20T Black Acetal (POM) Copolymer

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer PolyOne Corporation
Trade Name LubriOne™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne LubriOne™ AT-000/20T Black Acetal (POM) Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability.Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.52 g/cc
1.52 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.020 - 0.030 cm/cm
0.020 - 0.030 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.010 - 0.030 cm/cm
0.010 - 0.030 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 41.4 MPa
6000 psi
5.1 mm/min; ASTM D638
Tensile Strength, Yield 42.1 MPa
6110 psi
Type I, 5.1 mm/min; ASTM D638
Elongation at Break 15 %
15 %
Type I, 5.1 mm/min; ASTM D638
Tensile Modulus 1.65 GPa
239 ksi
Type I, 5.1 mm/min; ASTM D638
Flexural Strength 68.3 MPa
9910 psi
1.3 mm/min; ASTM D790
Flexural Modulus 1.86 GPa
270 ksi
1.3 mm/min; ASTM D790
Izod Impact, Notched 0.370 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
0.693 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Injection Molded; ASTM D256
Coefficient of Friction, Dynamic 0.098
0.098
vs. Steel - Dynamic; ASTM D1894
Coefficient of Friction, Static 0.11
0.11
vs. Steel - Static; ASTM D1894
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 151 °C

@Thickness 6.35 mm
304 °F

@Thickness 0.250 in
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 82.8 °C

@Thickness 6.35 mm
181 °F

@Thickness 0.250 in
Unannealed; ASTM D648
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL 94
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
UL 94
Descriptive Properties Value Comments
Features Copolymer
Good Wear Resistance
Low Friction
Lubricated
Forms Pellets
Generic Material Acetal (POM) Copolymer
Generic Name Acetal (POM) Copolymer
Processing Method Injection Molding
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
RoHS Compliance RoHS Compliant
Uses Appliance Components
Automotive Applications
Bearings
Business Equipment
Consumer Applications
Conveyor Parts
Gears
Industrial Applications
Printer Parts
Pulleys
Rollers