Plastcom SLOVAMID 66 GF 30 FRA 5 Polyamide 66, 30% Glass Fiber, Halogen Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled , Nylon 66, Glass Fiber Filled, Flame Retardant
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVAMID
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVAMID 66 GF 30 FRA 5 Polyamide 66, 30% Glass Fiber, Halogen Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FeaturesPA 66 for injection moulding, reinforced with 30% glass fiber and halogen flame retardant. Application in electrical industry: breakers, coil forms, covers, terminals. Slightly decreased flammability, glow wire 960°C.Application: Injection MouldingInformation Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.49 g/cc
0.0538 lb/in³
STN 64 0111
Linear Mold Shrinkage 0.0048 cm/cm
0.0048 in/in
STN 64 0808
Linear Mold Shrinkage, Transverse 0.0085 cm/cm
0.0085 in/in
STN 64 0808
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
STN EN ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 150 MPa
21800 psi
STN EN ISO 527-2
Elongation at Break 2.0 %
2.0 %
STN EN ISO 527-2
Tensile Modulus 9.50 GPa
1380 ksi
STN EN ISO 527-2
Flexural Strength 220 MPa
31900 psi
STN EN ISO 178
Flexural Modulus 7.60 GPa
1100 ksi
STN EN ISO 178
Charpy Impact Unnotched 5.00 J/cm²

@Temperature -20.0 °C
23.8 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
5.50 J/cm²

@Temperature 23.0 °C
26.2 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Charpy Impact, Notched 0.900 J/cm²

@Temperature -20.0 °C
4.28 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
1.00 J/cm²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Thermal Properties Metric English Comments
Melting Point 260 °C
500 °F
DSC; STN EN ISO 3146
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
STN EN ISO 75/A
Vicat Softening Point 250 °C
482 °F
B; STN EN ISO 306
Flammability, UL94 V-0
V-0
Glow Wire Test 960 °C
1760 °F
STN IEC 60695-2-10
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+17 ohm-cm
1.00e+17 ohm-cm
STN IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
STN IEC 60093
Dielectric Strength 40.0 kV/mm
1020 kV/in
STN IEC 60243
Comparative Tracking Index 450 V
450 V
STN 34 6468
Processing Properties Metric English Comments
Melt Temperature 280 - 300 °C
536 - 572 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4 hour
4 hour
Moisture Content 0.15 %
0.15 %
STN EN ISO 960
Injection Pressure 70.0 - 120 MPa
10200 - 17400 psi