PTS Tristar® PC-10GFR 10% Glass Reinforced Polycarbonate With Release

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Glass Fiber Filled, Flame Retardant
Manufacturer Polymer Technology & Services, LLC (PTS)
Trade Name Tristar®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PTS Tristar® PC-10GFR 10% Glass Reinforced Polycarbonate With Release.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
Physical Properties Metric English Comments
Density 1.25 g/cc
0.0452 lb/in³
ASTM D792
Water Absorption 0.12 %
0.12 %
24 hours at 73°F; ASTM D570
Linear Mold Shrinkage 0.0020 - 0.0040 cm/cm

@Thickness 3.17 mm
 0.0020 - 0.0040 in/in

@Thickness 0.125 in
 ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ASTM D785
Tensile Strength, Yield 62.0 MPa

@Thickness 3.17 mm
 8990 psi

@Thickness 0.125 in
 ASTM D638
Elongation at Break 15 %

@Thickness 3.17 mm
 15 %

@Thickness 0.125 in
 ASTM D638
Flexural Yield Strength 96.5 MPa

@Thickness 3.17 mm
 14000 psi

@Thickness 0.125 in
 ASTM D790
Flexural Modulus 3.10 GPa

@Thickness 3.17 mm
 450 ksi

@Thickness 0.125 in
 ASTM D790
Izod Impact, Notched 1.07 J/cm

@Thickness 3.17 mm
 2.00 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Tensile Impact Strength 53.3 kJ/m²

@Thickness 3.17 mm
 25.4 ft-lb/in²

@Thickness 0.125 in
 ASTM D1822
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 138 °C
280 °F
ASTM D648
UL RTI, Electrical 80.0 °C
176 °F
125 °C
257 °F
UL RTI, Mechanical with Impact 80.0 °C
176 °F
115 °C
239 °F
UL RTI, Mechanical without Impact 80.0 °C
176 °F
125 °C
257 °F
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
5VA

@Thickness 2.40 mm
 5VA

@Thickness 0.0945 in
Oxygen Index 37.1 %
37.1 %
ASTM D2863
Glow Wire Test 875 °C
1610 °F
GWIT
960 °C
1760 °F
GWFI
Electrical Properties Metric English Comments
Volume Resistivity 3.00e+15 ohm-cm
3.00e+15 ohm-cm
after 96 hours at 90°C, 50% RH; ASTM D257
6.00e+15 ohm-cm
6.00e+15 ohm-cm
after 40 hours at 23°C, 50% RH; ASTM D257
Dielectric Strength 19.0 kV/mm

@Thickness 3.00 mm
 483 kV/in

@Thickness 0.118 in
 ASTM D149
Arc Resistance 0.00 - 60 sec
0.00 - 60 sec
PLC 7
60 - 120 sec
60 - 120 sec
PLC 6
Comparative Tracking Index 100 - 175 V
100 - 175 V
PLC 4
175 - 250 V
175 - 250 V
PLC 3
Hot Wire Ignition, HWI 30 - 60 sec
30 - 60 sec
PLC 2
60 - 120 sec
60 - 120 sec
PLC 1
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
PLC 0
>= 120 arcs
>= 120 arcs
PLC 0
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
PLC 3