PTS Tristar® PC-10 10 MFI Extrusion Grade Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Extruded |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | Tristar® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS Tristar® PC-10 10 MFI Extrusion Grade Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | 24 hours at 73°F; ASTM D570 |
| Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 62.1 MPa @Thickness 3.17 mm |
9010 psi @Thickness 0.125 in |
ASTM D638 |
| Elongation at Break | 100 % @Thickness 3.17 mm |
100 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Yield Strength | 89.6 MPa @Thickness 3.17 mm |
13000 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 2.21 GPa @Thickness 3.17 mm |
321 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 6.41 J/cm @Thickness 3.17 mm |
12.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.2 µm/m-°C @Temperature -40.0 - 95.0 °C |
39.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E831-06 |
| CTE, linear, Transverse to Flow | 68.4 µm/m-°C @Temperature -40.0 - 95.0 °C |
38.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E831-06 |
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 266 - 277 °C | 510 - 530 °F | |
| Middle Barrel Temperature | 271 - 282 °C | 520 - 540 °F | |
| Front Barrel Temperature | 282 - 299 °C | 540 - 570 °F | |
| Nozzle Temperature | 277 - 304 °C | 530 - 580 °F | |
| Melt Temperature | 288 - 316 °C | 550 - 600 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | 48 hours max. |
| Injection Pressure | 82.7 - 124 MPa | 12000 - 18000 psi | |
| Back Pressure | 0.345 - 1.38 MPa | 50.0 - 200 psi | |
| Clamp Pressure | 27.6 - 68.9 MPa | 4000 - 10000 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed- Edge Gate | Slow to Medium | |
| Injection Speed- Tab Gate | Medium to Fast | |
| Injection Speed- Tunnel Gate | Fast |
Users viewing this material also viewed the following:
- Nye Lubricants 789DM (RL) Synthetic Oil
- Rogers Corporation RT/duroid® 6035HTC Ceramic Filled PTFE Composite, High Power RF and Microwave
- SABIC Innovative Plastics Lexan® HF1140 PC (Asia Pacific)
- Lord Adhesives Thermosetâ„¢ MD-140 Conductive Adhesive
- Lotte Chemical Titan TITANEX® HB0972 High density polyethylene Hexene-1 resin
- SABIC Innovative Plastics LNP Stat-kon ZE0039 MODIFIED POYPHENYLENE (Asia Pacific)
- Teknor Apex Monprene® MP 1049 Thermoplastic Elastomer
- Tra-Con Tra-Cast 3104 Low Viscosity Epoxy Casting Compound
- DSM Arnitel® VT3108 TPC-ET
- Arlon R37480X008 0.008" (0.203 mm) Uncured Silicone Rubber with Substrate: PTFE Coated Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved