| Category | Polymer , Thermoplastic , Fluoropolymer , PTFE |
| Manufacturer | Adamas |
| Trade Name | Adalon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Adamas Adalon® 406 PTFE, 15% PEEK.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Adamas, HPM
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.93 - 1.96 g/cc | 1.93 - 1.96 g/cc | ASTM D792 |
| Deformation | 5.5 - 7.5 % | 5.5 - 7.5 % | Permanent deformation after 24 hrs @ 23°C; ASTM D621 |
| 5.0 - 12 % | 5.0 - 12 % | ASTM D621 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 57 - 62 | 57 - 62 | ASTM D2240 |
| Ball Indentation Hardness | 50.0 - 55.0 MPa | 7250 - 7980 psi | ISO 2032-N132 |
| Tensile Strength at Break | >= 13.0 MPa | >= 1890 psi | ASTM D4745-97 |
| Elongation at Break | >= 130 % | >= 130 % | ASTM D4745-97 |
| Compressive Strength | 5.50 - 7.50 MPa @Temperature 23.0 °C, Time 86400 sec |
798 - 1090 psi @Temperature 73.4 °F, Time 24.0 hour |
@ 1% deformation, 140 Kg/cm<sup>2</sup>; ASTM D621 |
| Coefficient of Friction, Dynamic | 0.15 - 0.19 | 0.15 - 0.19 | ASTM D1894 |
| Coefficient of Friction, Static | 0.20 - 0.45 | 0.20 - 0.45 | ASTM D1894 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.350 W/m-K | 2.43 BTU-in/hr-ft²-°F | ASTM C 177 |
| Melting Point | 327 °C | 621 °F | DSC |
| Maximum Service Temperature, Air | 250 °C | 482 °F | DSC |
| Minimum Service Temperature, Air | -85.0 °C | -121 °F | DSC |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D257 |
| Dielectric Constant | 1.9 @Frequency 60.0 - 2.00e+6 Hz |
1.9 @Frequency 60.0 - 2.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 20.0 - 60.0 kV/mm | 508 - 1520 kV/in | ASTM D149 |
Users viewing this material also viewed the following:
- Polymer Resources PPX-GP7 Modified-PPO, General Purpose
- SABIC Innovative Plastics Lexan® ML7686 PC (Asia Pacific)
- PolyOne Geon™ Vinyl Cellular E8202 Polyvinyl Chloride, Rigid (PVC, Rigid)
- MF-5062 Polyurethane-based Biomedical Elastomer
- Rogers Corporation Bisco™ FPC Cellular Silicone Foam
- SABIC HP0322N Low Density Polyethylene for Blown Film
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 0.5 PHR Zinc Stearate
- Kraton® G1657 + PA-6,6 blend (12/8/80)
- Plenco 2571 Phenolic, Granular, Injection Molded
- BASF Ultramid® A3W2G6 BK 20560 30% Glass Filled PA66 (Dry)
Copyright © lookpolymers.com All Rights Reserved