PTS Trilac® ABS-MP1000 Metal Plating Grade ABS Resin
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Plating Grade |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | Trilac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS Trilac® ABS-MP1000 Metal Plating Grade ABS Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Melt Flow | 23 g/10 min @Load 10.0 kg, Temperature 220 °C |
23 g/10 min @Load 22.0 lb, Temperature 428 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 103 | 103 | ASTM D785 |
| Tensile Strength, Yield | 44.8 MPa | 6500 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Flexural Yield Strength | 73.1 MPa | 10600 psi | ASTM D790 |
| Flexural Modulus | 2.25 GPa | 326 ksi | ASTM D790 |
| Izod Impact, Notched | 2.94 J/cm @Thickness 3.17 mm |
5.51 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 193 °C | 380 °F | |
| Middle Barrel Temperature | 216 °C | 420 °F | |
| Front Barrel Temperature | 232 °C | 450 °F | |
| Melt Temperature | 218 - 260 °C | 425 - 500 °F | Nozzle temp not greater than stock |
| Mold Temperature | 48.9 - 65.6 °C | 120 - 150 °F | |
| Drying Temperature | 87.8 - 93.3 °C | 190 - 200 °F | |
| Dry Time | 2 - 24 hour | 2 - 24 hour | |
| Injection Pressure | 68.9 - 82.7 MPa | 10000 - 12000 psi | |
| Back Pressure | 0.689 MPa | 100 psi | |
| Screw Speed | 50 - 60 rpm | 50 - 60 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Fill Speed | Slow to Moderate |
Users viewing this material also viewed the following:
- M Chemical GUARD DOGâ„¢ UV360 Light Absorber
- Materion Beryllium Copper Alloy M25 Rod and Bar; H (TD04) Temper; up to 9.5 mm (UNS C17300)
- Karina E 42/6-FC-LMP Red Color Concentrate for PVC
- Techmer ES HiFill® PA6 GF15 L BK 15% Glass Filled
- Teknor Apex MF-87-L081A Polyvinyl Chloride, Flexible Film
- Chevron Phillips MarFlex® D139 m-LLDPE Linear Low Density Polyethylene
- Aaron Industries AAROLENE® ARPS 100-1 GPPS BLACK Polystyrene Compounded Resin
- 3M 8560 Cold Shrink Silicone Rubber 3/C Cable Breakout Boots
- Asahi Kasei Thermylene® P6-20FG-0754 20% Glass, Heat Stabilized
Copyright © lookpolymers.com All Rights Reserved