CP-Polymer-Technik Wellamid® 6000 GV 20 HWCP 20% Glass Fiber Nylon 6, Heat Stabilized, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | CP-Polymer-Technik GmbH & Co. |
| Trade Name | Wellamid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CP-Polymer-Technik Wellamid® 6000 GV 20 HWCP 20% Glass Fiber Nylon 6, Heat Stabilized, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by CP-Polymer-Technik GmbH & Co. KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.0 - 2.5 % | 2.0 - 2.5 % | 23°C/50%RH; DIN 53495 |
| Linear Mold Shrinkage | 0.0030 cm/cm @Thickness 4.00 mm |
0.0030 in/in @Thickness 0.157 in |
|
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Thickness 4.00 mm |
0.0090 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 140 MPa | 20300 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 7.10 GPa | 1030 ksi | ISO 527 |
| Flexural Modulus | 6.00 GPa | 870 ksi | DIN 52457 |
| Charpy Impact Unnotched | 7.30 J/cm² @Temperature 23.0 °C |
34.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 25.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
13.9 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 53752 |
| Melting Point | 215 °C | 419 °F | Kofler |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 179 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 179 |
| Vicat Softening Point | 200 °C | 392 °F | 50 N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
Stufe; IEC 707 |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
Stufe; IEC 707 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | ISO 3915 |
| Dielectric Constant | 4.0 @Frequency 1e+6 Hz |
4.0 @Frequency 1e+6 Hz |
IEC 250 |
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | IEC 243-1 |
| Dielectric Loss Index | 0.025 | 0.025 | At 1 MHz; IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | Stufe; IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 280 °C | 482 - 536 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Holding Pressure | High | |
| Injection Speed | Medium to High | |
| Screw Speed | High |
Users viewing this material also viewed the following:
- PolyOne Elastamax™ EG-9182 Thermoplastic Elastomer (TPE)
- SABIC Innovative Plastics LNP LUBRICOMP DFL369XF PC
- Nilit FRIANYL A63 HH-FK 2020 Nylon 6.6 for injection molding, 20% glass fiber and 20% glass ball reinforced
- SIDPEC EGYPTENE® HD 5813 EA HDPE Injection Molding
- Universal Wire Works Hastelloy W (AMS 5786) Filler Metal
- Valley Adhesives EM-800 High Temperature Application Glue Stick
- Goodfellow Copper 70/Iron 30 Alloy
- Zircar Refractory Composites SIL-1 Silica Cloth
- A. Schulman VOLOY™ 462 Hybrid Reinforced PBT Alloy
Copyright © lookpolymers.com All Rights Reserved