SABIC Innovative Plastics LNP THERMOCOMP RF008 PA 66 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF008 PA 66 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP Thermocomp RF008 is a compound based on PA66 resin containing glass fiber. It is used in many applications requiring high strength over weight performance. Also known as Thermocomp RF-1008
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 |
| 1.48 g/cc | 0.0535 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.600 % | 0.600 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm @Time 86400 sec |
0.013 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 185 MPa | 26800 psi | Type I, 5 mm/min; ASTM D638 |
| 188 MPa | 27300 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 |
| 2.7 % | 2.7 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 12.2 GPa | 1770 ksi | 1 mm/min; ISO 527 |
| 13.3 GPa | 1930 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 275 MPa | 39900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 10.4 GPa | 1510 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 12.1 GPa | 1750 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.17 J/cm | 2.19 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.2 J/cm | 21.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 74.0 kJ/m² | 35.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 26.8 µm/m-°C @Temperature 23.0 - 60.0 °C |
14.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| 27.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 59.2 µm/m-°C @Temperature 23.0 - 60.0 °C |
32.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| 59.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 253 °C @Thickness 3.20 mm |
487 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Rogers Corporation Poron® ThinStik Soft Seal 15-06030 Self-Adhesive Urethane Foam
- Kennametal Stellite Deloro® 716 PM with P/M Processing
- Taiwan Sheen Soon Sheenthane® AH-573 TPU for Hotmelt Adhesive
- Techno Polymer Techno ABS LM100 Transparent
- A. Schulman PP 3490-01G Polypropylene Homopolymer Polypropylene
- CP-Polymer-Technik Wellamid® 6600 MR 209 HWCP 20% Mineral Nylon 66, Heat Stabilized, Dry
- Daikin NEOFLON NP-30 FEP Pellets
- ACC EP RAP-1567 SP-HX EPI Engineered Polymers Silicone Aliphatic Polyurea
- Amco PRIMATOP HDPE RP 011 Granular High Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved