PTS PPE-LXS 314-10 PPE-HIPS, 10% Glass Filled
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) , Polystyrene + Polyphenylene Ether, Glass Filler |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS PPE-LXS 314-10 PPE-HIPS, 10% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Typical Applications: Water industrial partsInformation provided by PTS LLC.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Water Absorption | 0.10 % @Temperature 23.0 °C, Time 86400 sec |
0.10 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D955 |
| Melt Flow | 21 g/10 min @Load 5.00 kg, Temperature 300 °C |
21 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | type I; ASTM D638 |
| Elongation at Break | 10 % | 10 % | type I; ASTM D638 |
| Flexural Strength | 110 MPa | 16000 psi | 2.6 mm/min; ASTM D790 |
| Flexural Modulus | 3.20 GPa | 464 ksi | 2.6 mm/min; ASTM D790 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C @Thickness 6.40 mm |
248 °F @Thickness 0.252 in |
ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8961 (UF) Synthetic Oil
- Process Technologies Inc Tyfluor™ 1000 Sanitary Gasket
- Qualchem Danamid FEW-25 Polyamide 6, 25% Mineral Filled
- Kennametal Stellite Nucalloy® 45 (Stoody® 45) Nickel-Chromium-Boron Alloy
- Materion Beryllium Copper Alloy 165 Rod and Bar; HT (TH04) Temper; over 25.4 to 76 mm (UNS C17000)
- LG Chemical LI942 Heat Resistant ASA
- Gouda Vuurvast GOLITE 135 L Refractory Insulating Castable
- American Elements Platinum Nanoparticles
- Bhansali Engineering Abstron MIF-45 ABS Injection Molding Grade
- Techmer ES HiFill FR® PA6/6 GF30 FR HS L 30% Glass Filled
Copyright © lookpolymers.com All Rights Reserved