Ascend Performance Materials Vydyne® R515H Nylon 66, 15% Glass Reinforced, Conditioned

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® R515H Nylon 66, 15% Glass Reinforced, Conditioned.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vydyne® R515H is general-purpose, heat-stabilized, hydrolysis-resistant, 15% glass-fiber reinforced PA66 resin. Available in natural it is specifically designed to maximize the retention of physical properties when exposed to anti-freeze solutions at elevated temperatures. This product is also lubricated for improved flow and offers superior surface appearance. Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep, and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluid and most solvents. Vydyne R515H is heat-stabilized to minimize oxidative degradation of the polymer when exposed to elevated temperatures in service. This product provides improved retention of physical properties under exposure to long-term heat. Also Vydyne R515H has excellent knit-line strength and fatigue resistance, which is essential for cycle testing with anti-freeze solutions. Typical Applications/End uses: Vydyne R515H is successfully mused in a wide range of injection molding engineering applications, including automotive clips, radiator end tanks, parts of the air-conditioning and petrol distribution system, etc. (under the hood); electrical connectors, housings, bobbins, etc.; and industrial applications such as gears, bearing shells, covers, housings, etc.Availability:Asia PacificEuropeNorth AmericaFiller/Reinforcement:Glass Fiber, 15% Filler by WeightAdditive:Heat StabilizerLubricant Features: Gasoline ResistanceGood Chemical ResistanceGood FlowGood Mold ReleaseGrease ResistantHeat StabilizedHigh RigidityHigh StrengthLubricatedOil ResistantSolvent ResistantUses:Automotive Under the HoodGearsHousingsPower/Other ToolsAppearance: Natural ColorForms: PelletsProcessing Method: Injection MoldingInformation provided by Ascend Performance Materials.
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
ISO 1183
Water Absorption 1.0 %

@Time 86400 sec
1.0 %

@Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 2.2 %
2.2 %
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0050 cm/cm

@Diameter 2.00 mm
0.0050 in/in

@Diameter 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.010 cm/cm

@Diameter 2.00 mm
0.010 in/in

@Diameter 0.0787 in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 80.0 MPa
11600 psi
ISO 527-2
Elongation at Break 13 %
13 %
ISO 527-2
Tensile Modulus 4.00 GPa
580 ksi
ISO 527-2
Flexural Strength 110 MPa
16000 psi
ISO 178
Flexural Modulus 3.25 GPa
471 ksi
ISO 178
Izod Impact, Notched (ISO) 5.40 kJ/m²

@Temperature -30.0 °C
2.57 ft-lb/in²

@Temperature -22.0 °F
ISO 180
7.00 kJ/m²

@Temperature 23.0 °C
3.33 ft-lb/in²

@Temperature 73.4 °F
ISO 180
Charpy Impact Unnotched 3.80 J/cm²

@Temperature -30.0 °C
18.1 ft-lb/in²

@Temperature -22.0 °F
ISO 179
4.30 J/cm²

@Temperature 23.0 °C
20.5 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Charpy Impact, Notched 0.530 J/cm²

@Temperature -30.0 °C
2.52 ft-lb/in²

@Temperature -22.0 °F
ISO 179
0.750 J/cm²

@Temperature 23.0 °C
3.57 ft-lb/in²

@Temperature 73.4 °F
ISO 179