C.O.I.M. LARIPUR® LPR5020 Standard Adipate Ester Polyurethane

Category	Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer , Polyurethane, TP
Manufacturer	C.O.I.M. S.p.A.
Trade Name	Laripur®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	C.O.I.M. LARIPUR® LPR5020 Standard Adipate Ester Polyurethane.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: The products of the LARIPUR® line are thermoplastic polyurethanes. These products combine the technology of thermoplastic products with the features of polyurethanes:Excellent abrasion resistanceGreat flexibility with constancy at temperature variationsGood compression resistanceGood water and light resistanceGood resistance to oils, fats and to many types of solventsSeries 20 Standard Adipate Ester: These products are based on saturated polyesters. They exhibit strength and durability with excellent tear and abrasion resistance; good hydrolytic stability resistance to solvents, oxidation and UV light degradation.Information provided by P.A.T. Products, Inc.

Physical Properties	Metric	English	Comments
Specific Gravity	1.23 g/cc	1.23 g/cc	ASTM D792

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	50	50	ASTM D2240
Tensile Strength, Yield	58.1 MPa	8430 psi	ASTM D412
Elongation at Break	470 %	470 %	ASTM D412
50% Modulus	0.00820 GPa	1.19 ksi	ASTM D412
100% Modulus	0.0106 GPa	1.54 ksi	ASTM D412
300% Modulus	0.0268 GPa	3.89 ksi	ASTM D412
Flexural Modulus	0.0750 GPa	10.9 ksi	ASTM D790
Tear Strength	123 kN/m	702 pli	ASTM D624
Abrasion	35	35	mm3, Abrasion Loss; DIN 53516
Compression Set	24 %	24 %	70 hours at 23°C; ASTM D395
	50 % @Temperature 70.0 °C	50 % @Temperature 158 °F	Method B, 22 hours; ASTM D395
Torsional Stiffness	20.0 MPa	2900 psi	+20°C; ASTM D1043
	190 MPa	27600 psi	-20°C; ASTM D1043

Thermal Properties	Metric	English	Comments
Vicat Softening Point	105 °C	221 °F	ASTM D1525