Overview of materials for Polypropylene, Glass Reinforced, Impact Modified

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Glass Reinforced, Impact Modified
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polypropylene, Glass Reinforced, Impact Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Glass Reinforced, Impact Modified". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 0.960 - 1.44 g/cc
0.0347 - 0.0520 lb/in³
Average value: 1.12 g/cc Grade Count:37
Filler Content 10.0 - 40.0 %
10.0 - 40.0 %
Average value: 24.2 % Grade Count:18
Water Absorption 0.0100 - 0.0600 %
0.0100 - 0.0600 %
Average value: 0.0264 % Grade Count:14
Linear Mold Shrinkage 0.00100 - 0.0226 cm/cm
0.00100 - 0.0226 in/in
Average value: 0.00526 cm/cm Grade Count:33
Linear Mold Shrinkage, Transverse 0.00930 - 0.0210 cm/cm
0.00930 - 0.0210 in/in
Average value: 0.0140 cm/cm Grade Count:5
Melt Flow 0.900 - 16.0 g/10 min
0.900 - 16.0 g/10 min
Average value: 7.14 g/10 min Grade Count:17
Mechanical Properties Metric English Comments
Hardness, Rockwell R 80.0 - 115
80.0 - 115
Average value: 95.9 Grade Count:18
Tensile Strength, Ultimate 20.0 - 115 MPa
2900 - 16700 psi
Average value: 53.0 MPa Grade Count:31
Tensile Strength, Yield 31.0 - 95.0 MPa
4500 - 13800 psi
Average value: 64.4 MPa Grade Count:7
Elongation at Break 2.00 - 11.0 %
2.00 - 11.0 %
Average value: 5.55 % Grade Count:30
Elongation at Yield 0.600 - 2.50 %
0.600 - 2.50 %
Average value: 1.87 % Grade Count:3
Modulus of Elasticity 1.50 - 9.50 GPa
218 - 1380 ksi
Average value: 4.46 GPa Grade Count:23
Flexural Yield Strength 4.48 - 145 MPa
650 - 21000 psi
Average value: 75.9 MPa Grade Count:31
Flexural Modulus 1.50 - 7.85 GPa
218 - 1140 ksi
Average value: 4.04 GPa Grade Count:36
Izod Impact, Notched 0.518 - 2.14 J/cm
0.970 - 4.00 ft-lb/in
Average value: 1.24 J/cm Grade Count:30
1.30 - 1.30 J/cm

@Temperature -40.0 - -40.0 °C
2.44 - 2.44 ft-lb/in

@Temperature -40.0 - -40.0 °F
Average value: 1.30 J/cm Grade Count:2
Izod Impact, Unnotched 2.14 - 10.7 J/cm
4.00 - 20.0 ft-lb/in
Average value: 5.31 J/cm Grade Count:21
4.80 - 4.80 J/cm

@Temperature -40.0 - -40.0 °C
8.99 - 8.99 ft-lb/in

@Temperature -40.0 - -40.0 °F
Average value: 4.80 J/cm Grade Count:2
Izod Impact, Notched (ISO) 6.50 - 16.0 kJ/m²
3.09 - 7.61 ft-lb/in²
Average value: 11.0 kJ/m² Grade Count:4
Charpy Impact Unnotched 1.60 - 7.50 J/cm²
7.61 - 35.7 ft-lb/in²
Average value: 4.16 J/cm² Grade Count:7
1.00 - 4.70 J/cm²

@Temperature -20.0 - -20.0 °C
4.76 - 22.4 ft-lb/in²

@Temperature -4.00 - -4.00 °F
Average value: 2.98 J/cm² Grade Count:4
Charpy Impact, Notched 0.200 - 1.00 J/cm²
0.952 - 4.76 ft-lb/in²
Average value: 0.617 J/cm² Grade Count:6
0.100 - 0.800 J/cm²

@Temperature -20.0 - -20.0 °C
0.476 - 3.81 ft-lb/in²

@Temperature -4.00 - -4.00 °F
Average value: 0.425 J/cm² Grade Count:4
Thermal Properties Metric English Comments
Melting Point 145 - 168 °C
293 - 334 °F
Average value: 161 °C Grade Count:8
Deflection Temperature at 0.46 MPa (66 psi) 127 - 166 °C
260 - 331 °F
Average value: 150 °C Grade Count:26
Deflection Temperature at 1.8 MPa (264 psi) 67.0 - 160 °C
153 - 320 °F
Average value: 132 °C Grade Count:29
Vicat Softening Point 105 - 165 °C
221 - 329 °F
Average value: 151 °C Grade Count:7
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:18
Glow Wire Test 650 - 960 °C
1200 - 1760 °F
Average value: 857 °C Grade Count:3
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+14 - 1.00e+16 ohm-cm
1.00e+14 - 1.00e+16 ohm-cm
Average value: 7.08e+15 ohm-cm Grade Count:16
Surface Resistance 1.00e+12 - 1.00e+14 ohm
1.00e+12 - 1.00e+14 ohm
Average value: 6.70e+13 ohm Grade Count:3
Processing Properties Metric English Comments
Processing Temperature 193 - 227 °C
380 - 440 °F
Average value: 211 °C Grade Count:15
Melt Temperature 170 - 250 °C
338 - 482 °F
Average value: 225 °C Grade Count:8
Mold Temperature 32.2 - 80.0 °C
90.0 - 176 °F
Average value: 52.3 °C Grade Count:19
Injection Pressure 68.9 - 120 MPa
10000 - 17400 psi
Average value: 88.1 MPa Grade Count:18