Huntsman Rexell® M3109 Blown Film Extrusion LLDPE (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Huntsman Rexell® M3109 Blown Film Extrusion LLDPE (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Linear-low medium density copolymer and FDA compliant.Features: Excellent combination of stiffness, heat resistance, and impermeability to water vapor.Applications: Food packaging, multi-layer systems, and personal care films.FDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (c)3.2.aFilm properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation

Physical Properties	Metric	English	Comments
Density	0.940 g/cc	0.0340 lb/in³	ASTM D1505
Thickness	25.4 microns	1.00 mil
Melt Flow	4.0 g/10 min	4.0 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	660 %	660 %	ASTM D882
Film Elongation at Break, TD	870 %	870 %	ASTM D882
Secant Modulus, MD	0.406 GPa	58.9 ksi	ASTM D882
Secant Modulus, TD	0.520 GPa	75.4 ksi	ASTM D882
Elmendorf Tear Strength MD	420 g	420 g	ASTM D1922
Elmendorf Tear Strength TD	490 g	490 g	ASTM D1922
Elmendorf Tear Strength, MD	16.5 g/micron	420 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	19.3 g/micron	490 g/mil	ASTM D1922
Dart Drop	1.57 g/micron	40.0 g/mil	ASTM D1709
Dart Drop Test	40.0 g	0.0882 lb	ASTM D1709
Film Tensile Strength at Break, MD	29.0 MPa	4210 psi	ASTM D882
Film Tensile Strength at Break, TD	26.0 MPa	3770 psi	ASTM D882

Optical Properties	Metric	English	Comments
Haze	2.7 %	2.7 %	ASTM D1003
Gloss	90 %	90 %	at 45°; ASTM D523

Processing Properties	Metric	English	Comments
Melt Temperature	260 - 290 °C	500 - 554 °F