Overview of materials for Acetal Copolymer, 10% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 10% Glass Fiber Reinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Acetal Copolymer, 10% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, 10% Glass Fiber Reinforced". Specific grades with glass content between 5% and 14% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.20 - 1.58 g/cc
0.0434 - 0.0571 lb/in³
Average value: 1.47 g/cc Grade Count:47
Filler Content 5.00 - 10.0 %
5.00 - 10.0 %
Average value: 8.75 % Grade Count:8
Water Absorption 0.100 - 0.260 %
0.100 - 0.260 %
Average value: 0.211 % Grade Count:15
Moisture Absorption at Equilibrium 0.100 - 0.350 %
0.100 - 0.350 %
Average value: 0.245 % Grade Count:7
Water Absorption at Saturation 0.200 - 0.850 %
0.200 - 0.850 %
Average value: 0.690 % Grade Count:5
Linear Mold Shrinkage 0.00500 - 0.0300 cm/cm
0.00500 - 0.0300 in/in
Average value: 0.0112 cm/cm Grade Count:34
Linear Mold Shrinkage, Transverse 0.0100 - 0.0227 cm/cm
0.0100 - 0.0227 in/in
Average value: 0.0139 cm/cm Grade Count:9
Melt Flow 1.00 - 25.9 g/10 min
1.00 - 25.9 g/10 min
Average value: 11.0 g/10 min Grade Count:15
Mechanical Properties Metric English Comments
Hardness, Rockwell M 82.0 - 85.0
82.0 - 85.0
Average value: 84.0 Grade Count:3
Hardness, Rockwell R 80.0 - 110
80.0 - 110
Average value: 97.5 Grade Count:10
Ball Indentation Hardness 110 - 211 MPa
16000 - 30600 psi
Average value: 174 MPa Grade Count:3
Tensile Strength, Ultimate 44.8 - 110 MPa
6500 - 16000 psi
Average value: 74.2 MPa Grade Count:32
Tensile Strength, Yield 42.0 - 98.1 MPa
6090 - 14200 psi
Average value: 67.9 MPa Grade Count:17
Elongation at Break 1.50 - 20.0 %
1.50 - 20.0 %
Average value: 4.92 % Grade Count:43
Elongation at Yield 2.30 - 12.0 %
2.30 - 12.0 %
Average value: 6.52 % Grade Count:5
Modulus of Elasticity 2.40 - 8.50 GPa
348 - 1230 ksi
Average value: 4.67 GPa Grade Count:29
Flexural Yield Strength 68.9 - 147 MPa
10000 - 21300 psi
Average value: 109 MPa Grade Count:35
Flexural Modulus 2.40 - 8.50 GPa
348 - 1230 ksi
Average value: 4.10 GPa Grade Count:40
Izod Impact, Notched 0.267 - 0.801 J/cm
0.500 - 1.50 ft-lb/in
Average value: 0.526 J/cm Grade Count:32
Izod Impact, Unnotched 3.47 - 8.01 J/cm
6.50 - 15.0 ft-lb/in
Average value: 5.06 J/cm Grade Count:16
Izod Impact, Notched (ISO) 3.00 - 6.20 kJ/m²
1.43 - 2.95 ft-lb/in²
Average value: 4.92 kJ/m² Grade Count:13
5.00 - 5.00 kJ/m²

@Temperature -30.0 - -30.0 °C
2.38 - 2.38 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 5.00 kJ/m² Grade Count:1
Izod Impact, Unnotched (ISO) 24.0 - 33.0 kJ/m²
11.4 - 15.7 ft-lb/in²
Average value: 28.4 kJ/m² Grade Count:5
Charpy Impact Unnotched 3.00 - 6.00 J/cm²
14.3 - 28.6 ft-lb/in²
Average value: 4.80 J/cm² Grade Count:5
4.50 - 6.00 J/cm²

@Temperature -30.0 - -30.0 °C
21.4 - 28.6 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 5.25 J/cm² Grade Count:4
Charpy Impact, Notched 0.320 - 0.850 J/cm²
1.52 - 4.05 ft-lb/in²
Average value: 0.475 J/cm² Grade Count:12
0.320 - 0.650 J/cm²

@Temperature -30.0 - -30.0 °C
1.52 - 3.09 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 0.443 J/cm² Grade Count:4
Dart Drop, Total Energy 5.00 - 6.00 J
3.69 - 4.43 ft-lb
Average value: 5.33 J Grade Count:3
Thermal Properties Metric English Comments
CTE, linear 30.0 - 110 µm/m-°C
16.7 - 61.1 µin/in-°F
Average value: 68.9 µm/m-°C Grade Count:12
CTE, linear, Transverse to Flow 80.0 - 120 µm/m-°C
44.4 - 66.7 µin/in-°F
Average value: 96.0 µm/m-°C Grade Count:5
Melting Point 162 - 185 °C
324 - 365 °F
Average value: 167 °C Grade Count:19
Deflection Temperature at 0.46 MPa (66 psi) 154 - 168 °C
310 - 335 °F
Average value: 163 °C Grade Count:17
Deflection Temperature at 1.8 MPa (264 psi) 89.0 - 177 °C
192 - 350 °F
Average value: 149 °C Grade Count:38
Vicat Softening Point 135 - 159 °C
275 - 318 °F
Average value: 150 °C Grade Count:3
Flammability, UL94 HB
HB
Grade Count:24
Electrical Properties Metric English Comments
Electrical Resistivity 2000 - 1.00e+17 ohm-cm
2000 - 1.00e+17 ohm-cm
Average value: 5.67e+15 ohm-cm Grade Count:20
Surface Resistance 1000 - 1.00e+16 ohm
1000 - 1.00e+16 ohm
Average value: 2.33e+15 ohm Grade Count:13
Dielectric Constant 3.80 - 4.50
3.80 - 4.50
Average value: 4.13 Grade Count:6
Dielectric Strength 17.7 - 35.0 kV/mm
450 - 889 kV/in
Average value: 23.9 kV/mm Grade Count:12
Dissipation Factor 0.00300 - 0.0150
0.00300 - 0.0150
Average value: 0.00783 Grade Count:6
Comparative Tracking Index 500 - 600 V
500 - 600 V
Average value: 580 V Grade Count:5
Processing Properties Metric English Comments
Processing Temperature 80.0 - 230 °C
176 - 446 °F
Average value: 168 °C Grade Count:15
Die Temperature 190 - 210 °C
374 - 410 °F
Average value: 197 °C Grade Count:7
Melt Temperature 20.0 - 371 °C
68.0 - 700 °F
Average value: 184 °C Grade Count:16
Mold Temperature 60.0 - 149 °C
140 - 300 °F
Average value: 95.9 °C Grade Count:16
Drying Temperature 79.4 - 135 °C
175 - 275 °F
Average value: 103 °C Grade Count:16
Moisture Content 0.150 %
0.150 %
Average value: 0.150 % Grade Count:7
Dew Point -31.7 °C
-25.0 °F
Average value: -31.7 °C Grade Count:4
Injection Pressure 60.0 - 140 MPa
8700 - 20300 psi
Average value: 95.5 MPa Grade Count:18