BASF Ultramid® TG7S BK-102 35% Glass Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® TG7S BK-102 35% Glass Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid TG7S is a 34% glass reinforced, heat stabilized, impact modified nylon 6 injection molding grade. It was developed to meet the demanding requirements of the first North American seat cushion pan/frame to be made of an engineering plastic as opposed to metal. TG7S exhibits improved strength, stiffness and notched properties.
Physical Properties Metric English Comments
Density 1.38 g/cc
0.0499 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM Data; MD
Melt Flow 6.0 g/10 min

@Load 5.00 kg,
Temperature 235 °C
6.0 g/10 min

@Load 11.0 lb,
Temperature 455 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 165 MPa
23900 psi
5mm/min; ISO 527
Elongation at Break 3.0 %
3.0 %
5mm/min; ISO 527
Flexural Modulus 8.40 GPa
1220 ksi
ISO Data
Izod Impact, Notched (ISO) 22.0 kJ/m²
10.5 ft-lb/in²
ISO Test
16.6 kJ/m²

@Temperature -40.0 °C
7.90 ft-lb/in²

@Temperature -40.0 °F
ISO Test
Charpy Impact, Notched 2.20 J/cm²
10.5 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 208 °C
406 °F
ISO 75
Descriptive Properties Value Comments
Color BK-102
Commercial Status Active America
Impact Modified Yes
Primary Processing Technique Injection Molding