Nilit Nilamid A G5 FR C4 25% Glass Fiber Reinforced, Flame Retardant PA66 (with Halogens)

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer	Nilit
Trade Name	Nilamid
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Nilit Nilamid A G5 FR C4 25% Glass Fiber Reinforced, Flame Retardant PA66 (with Halogens).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Nilamid A G5 FR C4 combines excellent mechanical performance with flame retardancy. The halogenated flame retardant system used in this product allows a wide range of colors. This product does not contain the flame retardants mentioned in the WEEE directive (PBB or PBDE). The product is used widely throughout the electrical and appliance industries for applications like pressure switches, circuit breaker housings, contactors, timers and programmers. Key characteristics: UL listed V0 at 3.0 and 0.8 mmUL listed GWIT 825 °C and GWFI 960°C at 0.8 mm, compliant with IEC 60335-4UL listed on CTI PCL 1 (CTI = 425 V)Excellent mechanical performanceColorable in light colorsEasy processing Information provided by NILIT.

Physical Properties	Metric	English	Comments
Density	1.58 g/cc	0.0571 lb/in³	ASTM D792, ISO 1183
Water Absorption	0.50 %	0.50 %	23°C, 24h in H<sub>2</sub>O; sim. ISO 62
Water Absorption at Saturation	4.0 %	4.0 %	sim. ISO 62
Linear Mold Shrinkage, Flow	0.0040 cm/cm	0.0040 in/in	Euronil
Linear Mold Shrinkage, Transverse	0.0070 cm/cm	0.0070 in/in	Euronil

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	125 MPa	18100 psi	ISO 527, ASTM D638
Elongation at Break	2.0 %	2.0 %
Tensile Modulus	8.00 GPa	1160 ksi	ISO 527, ASTM D638
Flexural Yield Strength	185 MPa	26800 psi	ISO 178, ASTM D790
	130 MPa @Temperature 90.0 °C	18900 psi @Temperature 194 °F	ISO 178, ASTM D790
Flexural Modulus	8.50 GPa	1230 ksi	ISO 178, ASTM D790
	4.80 GPa @Temperature 90.0 °C	696 ksi @Temperature 194 °F	ISO 178, ASTM D790
Izod Impact, Notched (ISO)	5.00 kJ/m² @Temperature -30.0 °C	2.38 ft-lb/in² @Temperature -22.0 °F	ISO 180/1A
	6.50 kJ/m² @Temperature 23.0 °C	3.09 ft-lb/in² @Temperature 73.4 °F	ISO 180/1A
Charpy Impact Unnotched	2.70 J/cm²	12.8 ft-lb/in²	ISO 179
	2.40 J/cm² @Temperature -30.0 °C	11.4 ft-lb/in² @Temperature -22.0 °F	ISO 179
Charpy Impact, Notched	0.600 J/cm²	2.86 ft-lb/in²	ISO 179
	0.500 J/cm² @Temperature -30.0 °C	2.38 ft-lb/in² @Temperature -22.0 °F	ISO 179

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	110 °C	230 °F	20,000 hr; IEC 216
Deflection Temperature at 0.46 MPa (66 psi)	250 °C	482 °F	ISO 75, ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	242 °C	468 °F	ISO 75, ASTM D648
Vicat Softening Point	240 °C	464 °F	49 N; ISO 306, ASTM D1525
	254 °C	489 °F	9.8 N; ISO 306, ASTM D1525
Flammability, UL94	V-0 @Thickness 0.800 mm	V-0 @Thickness 0.0315 in
	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in
	V-0 @Thickness 3.20 mm	V-0 @Thickness 0.126 in
Oxygen Index	36 %	36 %	ASTM D2863
Glow Wire Test	825 °C @Thickness 0.800 mm	1520 °F @Thickness 0.0315 in	Glow Wire Ignition Temperature; IEC 695-2-13
	875 °C @Thickness 3.20 mm	1610 °F @Thickness 0.126 in	Glow Wire Ignition Temperature; IEC 695-2-13
	960 °C @Thickness 3.20 mm	1760 °F @Thickness 0.126 in	Glow Wire Flammability Index; IEC 694-2-12
	960 °C @Thickness 0.800 mm	1760 °F @Thickness 0.0315 in	Glow Wire Flammability Index; IEC 694-2-12

Electrical Properties	Metric	English	Comments
Dielectric Strength	21.0 kV/mm @Thickness 2.00 mm	533 kV/in @Thickness 0.0787 in	ASTM D149
Comparative Tracking Index	275 V @Thickness 3.20 mm	275 V @Thickness 0.126 in	Sol. B; IEC 112, UL 746A
	400 V @Thickness 3.20 mm	400 V @Thickness 0.126 in	Sol. A; IEC 112, UL 746A

Processing Properties	Metric	English	Comments
Nozzle Temperature	275 - 285 °C	527 - 545 °F
Zone 1	260 - 280 °C	500 - 536 °F	hopper
Zone 2	260 - 280 °C	500 - 536 °F
Zone 3	270 - 280 °C	518 - 536 °F
Zone 4	275 - 285 °C	527 - 545 °F
Melt Temperature	275 - 290 °C	527 - 554 °F	Do not melt above 290°C
Mold Temperature	90.0 - 110 °C	194 - 230 °F	Preferred
Drying Temperature	80.0 - 85.0 °C	176 - 185 °F
Dry Time	4 hour	4 hour
Injection Pressure	70.0 - 100 MPa	10200 - 14500 psi

Descriptive Properties	Value	Comments
Clamping Force	in tons, 0.7 times the projected surface area in cm²
Flammability Rating	SE	FMVSS No. 302, 355x100x1 mm
Heat Resistance - Ball Test	OK	at 125°C, IEC 309
	OK	at 165°C, IEC 309
Holding Pressure	90 MPa
Needle Test	OK	IEC 695-2-2, 1 or 2 mm