SABIC Innovative Plastics LNP LUBRILOY R2000A PA 66

Category	Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP Lubriloy
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRILOY R2000A PA 66.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP LUBRILOY* R2000A is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant.

Physical Properties	Metric	English	Comments
Density	1.02 g/cc	0.0368 lb/inÂ³	ASTM D792
	1.02 g/cc	0.0368 lb/inÂ³	ISO 1183
Moisture Absorption	0.300 %	0.300 %	50% RH, 24 hrs; ASTM D570
	0.430 %	0.430 %	23Â°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.0257 cm/cm @Time 86400 sec	0.0257 in/in @Time 24.0 hour	ISO 294
	0.026 cm/cm @Time 86400 sec	0.026 in/in @Time 24.0 hour	ASTM D955
Linear Mold Shrinkage, Transverse	0.026 cm/cm @Time 86400 sec	0.026 in/in @Time 24.0 hour	ASTM D955
	0.026 cm/cm @Time 86400 sec	0.026 in/in @Time 24.0 hour	ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	43.0 MPa	6240 psi	ASTM D638
	43.0 MPa	6240 psi	ISO 527
Tensile Strength, Yield	43.0 MPa	6240 psi	ISO 527
	47.0 MPa	6820 psi	ASTM D638
Elongation at Break	29.6 %	29.6 %	ISO 527
	38.6 %	38.6 %	ASTM D638
Elongation at Yield	6.0 %	6.0 %	ASTM D638
	8.8 %	8.8 %	ISO 527
Tensile Modulus	1.99 GPa	289 ksi	50 mm/min; ASTM D638
	2.10 GPa	305 ksi	1 mm/min; ISO 527
Flexural Strength	67.0 MPa	9720 psi	ASTM D790
	69.0 MPa	10000 psi	ISO 178
Flexural Modulus	1.93 GPa	280 ksi	ASTM D790
	2.20 GPa	319 ksi	ISO 178
Izod Impact, Notched	0.740 J/cm	1.39 ft-lb/in	ASTM D256
Izod Impact, Unnotched	NB	NB	ASTM D4812
Izod Impact, Notched (ISO)	6.00 kJ/mÂ²	2.86 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	137 kJ/mÂ²	65.2 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	6.00 J	4.43 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Impact Test	1.00 J	0.738 ft-lb	Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic	0.31	0.31	ASTM D3702 Modified
Coefficient of Friction, Static	0.27	0.27	ASTM D3702 Modified
K (wear) Factor	24.2 x 10^-8 mmÂ³/N-M	12.0 x 10^-10 inÂ³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	66.0 Â°C @Thickness 3.20 mm	151 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	67.0 Â°C	153 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	62.0 Â°C @Thickness 3.20 mm	144 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	UL 94 by SABIC-IP