Nilit FRIANYL B63 TF-GV 1530 Nylon 6 for injection molding, 15% PTFE lubricated, 30% glass fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 TF-GV 1530 Nylon 6 for injection molding, 15% PTFE lubricated, 30% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| Water Absorption | 0.50 - 1.0 % | 0.50 - 1.0 % | ISO 62 |
| Water Absorption at Saturation | 5.0 - 6.0 % | 5.0 - 6.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0070 - 0.015 cm/cm | 0.0070 - 0.015 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 8.00 GPa | 1160 ksi | ISO 527 |
| Flexural Strength | 190 MPa | 27600 psi | ISO 178 |
| Flexural Modulus | 7.10 GPa | 1030 ksi | ISO 178 |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | DIN 53453 |
| NB | NB | ISO 179/1eU | |
| 4.60 J/cm² @Temperature -40.0 °C |
21.9 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | ISO 179/1eA |
| 1.40 J/cm² | 6.66 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 150 °C | 302 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 500 V | 500 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 OB Polyamide 6, Optically Brightened
- Lord Adhesives Metech 7600A Cermet Multilayer Dielectric Composition
- Michelman® U-Nyte™ Set 201 Solid epoxy powder
- Lucas-Milhaupt Black Flux Silver Brazing Flux
- Struktol TR 065 Blending Aid, Processing Additive
- Sax Polymers SAXALEN PPH305G30 Polypropylene Homopolymer, 30% Glass Filled
- Unifrax Fiberfrax® LDS AL-Moldable Moldable Insulation
- Unipetrol C4 Fraction
- Aclo Accucomp Polyacetal (POM) ACE093L Low Viscosity
- DuPont Performance Polymers Delrin® 500P NC010 Acetal Homopolymer (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved