- Nilit FRIANYL B63 HS-GV30 Nylon 6 for injection molding, 30% glass fiber reinforced
Nilit FRIANYL B63 HS-GV30 Nylon 6 for injection molding, 30% glass fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 HS-GV30 Nylon 6 for injection molding, 30% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6 for injection molding, high impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 - 2.0 % | 1.5 - 2.0 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 7.0 % | 6.0 - 7.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0090 - 0.016 cm/cm | 0.0090 - 0.016 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 130 MPa | 18900 psi | ISO 2039-1 |
| Tensile Strength at Break | 140 MPa | 20300 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Tensile Modulus | 8.00 GPa | 1160 ksi | ISO 527 |
| Flexural Strength | 170 MPa | 24700 psi | ISO 178 |
| Flexural Modulus | 6.50 GPa | 943 ksi | ISO 178 |
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | DIN 53453 |
| NB | NB | ISO 179/1eU | |
| 5.80 J/cm² @Temperature -40.0 °C |
27.6 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.80 J/cm² | 8.57 ft-lb/in² | DIN 53453 |
| 2.20 J/cm² | 10.5 ft-lb/in² | ISO 179/1eA | |
| 1.60 J/cm² @Temperature -40.0 °C |
7.61 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| 2.00 J/cm² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Nye Lubricants 176A (SO) Synthetic Oil
- Noltex Soarnol® DT2903 Ethylene Vinyl Alcohol Copolymer
- PolyOne Geon™ 170 Series 173 Polyvinyl Chloride Homopolymer (PVC Homopolymer)
- Lehmann & Voss LUVOCOM® 3-7723/ EG Polyamide 6, with carbon fiber, high viscosity
- Saint-Gobain CHR® 2995-11R Glass-Foil Backing Silicone Adhesive Pressure Sensitive Tape
- Styron CALIBREâ„¢ 200 15 Polycarbonate, General Purpose
- DuPont™ Fusabond® E158H Polymer Modifier
- Eurotec® Tecomid® NA40 MF40 BK001 HS PA6.6, 40% mineral filled, heat stabilized, black
- Wall Colmonoy COLMONOY® 42 SA - Hard Nickel-Chromium-Boron Alloy Containing Chromium Carbides
- Kraton® D1102 + PP blend (50/50)
Copyright © lookpolymers.com All Rights Reserved