A. Schulman COMTUF® 464 Glass Reinforced Impact Modified PBT Alloy
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Filled, Impact Modified |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman COMTUF® 464 Glass Reinforced Impact Modified PBT Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.67 g/cc | 1.67 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm @Thickness 3.175 mm |
0.0010 in/in @Thickness 0.1250 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 140 MPa | 20300 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 176 MPa | 25500 psi | ASTM D790 |
| Izod Impact, Notched | 0.854 J/cm | 1.60 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 222 °C | 432 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 260 °C | 482 - 500 °F | |
| Mold Temperature | 30.0 - 65.6 °C | 86.0 - 150 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
Users viewing this material also viewed the following:
- Formosa Plastics Formolene® L63565U Rotational Molding LLDPE (discontinued **)
- Indium Corp. NR-10-D Wave Solder Flux, No-Clean
- SABIC Innovative Plastics LNP LUBRICOMP DP003EH PC (Asia Pacific)
- Samsung Cheil Industries Starex® SF-301H Expandable Polystyrene (EPS) FR
- DSM Arnite® TV4 441 (PBT+PET)-GF20
- Arkema Group OREVAC® 18510 Grafted Maleic Anhydride Polyethylene
- Arlon 55148R036 0.036" (0.914 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- 3M AC-770 Class B-1 Aerospace Sealant
- PlastxWorld CEVIAN® A1500 PA/ABS Alloy, Conditioned
- Silberline Sparkle Silvet® 797-30-E1
Copyright © lookpolymers.com All Rights Reserved