Nilit FRIANYL B63 H-GV15 Nylon 6 for injection molding, 15% glass fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 H-GV15 Nylon 6 for injection molding, 15% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 - 2.6 % | 1.5 - 2.6 % | ISO 62 |
| Water Absorption at Saturation | 7.0 - 8.0 % | 7.0 - 8.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0070 - 0.014 cm/cm | 0.0070 - 0.014 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 155 MPa | 22500 psi | ISO 2039-1 |
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527 |
| Elongation at Break | 4.5 % | 4.5 % | ISO 527 |
| Tensile Modulus | 6.00 GPa | 870 ksi | ISO 527 |
| Flexural Strength | 190 MPa | 27600 psi | ISO 178 |
| Flexural Modulus | 4.70 GPa | 682 ksi | ISO 178 |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | DIN 53453 |
| 3.30 J/cm² @Temperature -40.0 °C |
15.7 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 115 °C | 239 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 450 V | 450 V | CTI 100; IEC 112 |
| 500 V | 500 V | CTI-M 100; IEC 112 |
Users viewing this material also viewed the following:
- Parker Chomerics Tecknit® 73-00008 Electrically Conductive Acrylic and Polyurethane Paint
- Lotte Chemical Titan TITANCEED® mL156 Linear low density polyethylene resin (discontinued **)
- SABIC Innovative Plastics Lexan® EXRL0627 PC Copolymer
- Lehmann & Voss LUVOCOM® 80-7112/BK Polyacetal-copolymer, with glass fiber and carbon fiber
- Lanxess Durethan® BM 240 H2.0 901510 Nylon 6, 40% Mineral
- Shinkong Synthetic Fibers Shinite® N602G6S Nylon 66, Fire Retardant
- Universal Wire Works ER90SB-9 Stainless Steel Bare Wire
- DuPont Teijin Films Mylar® RL32 Polyester Packaging Film, 100 Gauge
- BorsodChem ONGRONAT HS-44 MDI Isocyanate
- Ashley Polymers Ashlene® 279 PPO Alloy
Copyright © lookpolymers.com All Rights Reserved