SABIC Innovative Plastics LNP STAT-LOY ZF3021 PPE+PS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Stat-loy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-LOY ZF3021 PPE+PS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-LOY* ZF3021 is a compound based on PPE + PS Blend resin containing Glass Fiber. Added features include Antistatic, Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0060 cm/cm | 0.0010 - 0.0060 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 127 MPa | 18400 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 4.20 GPa | 609 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 132 MPa | 19100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.00 GPa | 580 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 152 °C | 306 °F | Rate B/120; ISO 306 |
| Flammability, UL94 | V-1 @Thickness 1.50 mm |
V-1 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | ASTM D257 |
| Dielectric Strength | 17.5 kV/mm @Thickness 3.20 mm |
445 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| 27.2 kV/mm @Thickness 1.60 mm |
691 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 | |
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 |
Users viewing this material also viewed the following:
- NOVA Chemicals DYLARK® 378 Impact Grade Engineering Resin
- Johnson Matthey JM6337 Soft Solder/Flux
- Wellman Wellamid® GFX1872-N1 (PTFE) Nylon 66, 33% Glass Reinforced, Lubricated
- A. Schulman POLYBATCH™ Red 5170 Concentrate Based In Polyethylene
- Lubrizol Estane® 2103-85AE Thermoplastic Polyurethane Elastomer
- Covestro Bayblend® T90 HT Polycarbonate + ABS
- Dow UNIVAL™ DMDD-6230 NT 7 High Density Polyethylene Resin (HDPE)
- Arlon 51586R040 0.040" (1.02 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Eurotec® Tecomid® NB50 BK001 IH PA6, impact modified, black, extrusion grade
Copyright © lookpolymers.com All Rights Reserved