DSM Arnite® AV2 370 HF PET-GF35
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 40% Glass Reinforced |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Arnite® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Arnite® AV2 370 HF PET-GF35.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
35% Glass Reinforced, Brake Booster Body Valves, High Flow
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | ISO 1183 |
| Water Absorption | 0.45 % | 0.45 % | Sim. To ISO 62 |
| Moisture Absorption | 0.180 % | 0.180 % | Sim. To ISO 62 |
| Viscosity | 12500 cP @Shear Rate 100000 1/s, Temperature 310 °C |
12500 cP @Shear Rate 100000 1/s, Temperature 590 °F |
|
| 15000 cP @Shear Rate 100000 1/s, Temperature 290 °C |
15000 cP @Shear Rate 100000 1/s, Temperature 554 °F |
||
| 17500 cP @Shear Rate 100000 1/s, Temperature 270 °C |
17500 cP @Shear Rate 100000 1/s, Temperature 518 °F |
||
| 110000 cP @Shear Rate 100 1/s, Temperature 310 °C |
110000 cP @Shear Rate 100 1/s, Temperature 590 °F |
||
| 175000 cP @Shear Rate 100 1/s, Temperature 290 °C |
175000 cP @Shear Rate 100 1/s, Temperature 554 °F |
||
| 250000 cP @Shear Rate 100 1/s, Temperature 270 °C |
250000 cP @Shear Rate 100 1/s, Temperature 518 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 200 MPa | 29000 psi | ISO 527-1/-2 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527-1/-2 |
| Tensile Modulus | 13.0 GPa | 1890 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.10 J/cm² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| 1.10 J/cm² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C | 13.9 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | ISO 11359-1/-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 |
| HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.7 @Frequency 100 Hz |
3.7 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0030 @Frequency 100 Hz |
0.0030 @Frequency 100 Hz |
IEC 60250 |
| 0.013 @Frequency 1.00e+6 Hz |
0.013 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 |
Users viewing this material also viewed the following:
- MV Labs PT780 Pt(NH3)4(NO3)2·xH2O Tetramineplatinum(II) nitrate
- Ineos ABS Lustran® ABS 150G22 20% Glass Fiber Reinforced Grade
- Teknor Apex Telcar® OBC 4545A Thermoplastic Elastomer
- Unipetrol PP MONSTEN® GB 802 Polypropylene Random Copolymer
- A. Schulman POLYBATCH™ White LL8855 GP Concentrate Based In LLDPE
- Dow BETAMATE™ 7000 fast curing polyurethane adhesive component
- DuPont Teijin Films Mylar® ADS Polyester Film, 200 Gauge
- Multibase Multi-Flam™ 0102 PP Polypropylene
Copyright © lookpolymers.com All Rights Reserved