Lehmann & Voss LUVOCOM® 6-7833 Polyamide 12, with PTFE, lubricant modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, PTFE Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 6-7833 Polyamide 12, with PTFE, lubricant modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Dynamic stressed parts.Low waterabsorbtion, for dimensional stable precision parts.Isotropic shrinkage characteristics.Bearings, sleeves, sliding elements, handles, machine parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0070 - 0.010 cm/cm | 0.0070 - 0.010 in/in | |
| Melt Flow | <= 11.4 g/10 min @Load 5.00 kg, Temperature 235 °C |
<= 11.4 g/10 min @Load 11.0 lb, Temperature 455 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 45.0 MPa | 6530 psi | |
| Elongation at Yield | 6.0 % | 6.0 % | |
| 8.0 % | 8.0 % | flexural | |
| Modulus of Elasticity | 2.30 GPa | 334 ksi | |
| Flexural Strength | 75.0 MPa | 10900 psi | |
| Flexural Modulus | 2.00 GPa | 290 ksi | |
| Charpy Impact Unnotched | 14.0 J/cm² | 66.6 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | |
| 140 °C | 284 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+9 ohm | >= 1.00e+9 ohm | |
| Insulation Resistance | >= 1.00e+9 ohm | >= 1.00e+9 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 °C | 482 °F | mass temp |
| Nozzle Temperature | 250 - 260 °C | 482 - 500 °F | |
| Zone 1 | 230 - 250 °C | 446 - 482 °F | |
| Zone 2 | 240 - 260 °C | 464 - 500 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |
| Drying Temperature | 75.0 °C @Time 21600 - 36000 sec |
167 °F @Time 6.00 - 10.0 hour |
Dehumidifying dryer |
| 105 °C @Time <=14400 sec |
221 °F @Time <=4.00 hour |
or |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- PSM Industries Ferro-TiC® PK Maraging Steel
- Ravago Manufacturing Americas Hylex® P1310G15 HB Polycarbonate, 15% Fiberglass Reinforced, UV Stabilized
- Teknor Apex Uniprene® UN-2023 Thermoplastic Elastomer
- Williams Advanced Alloys Wambraze™ WB718 Solder
- Eastman Embrace HY1000 Copolyester for Shrink Film
- Aclo Accutech Polypropylene Homopolymer HP0336C10L Calcium Reinforced
- Arkema Group BONDINE® HX 8290 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride
- Cheng Yu Plastic A703G25 ABS 25% Glass Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved