Nilit FRIANYL A63 N-SG5 Nylon 6.6 for injection molding, 5% mineral filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Mineral Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 N-SG5 Nylon 6.6 for injection molding, 5% mineral filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding, low viscosity.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 - 2.3 % | 1.5 - 2.3 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 8.0 % | 6.0 - 8.0 % | ISO 62 |
| Viscosity Measurement | 140 | 140 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.015 - 0.022 cm/cm | 0.015 - 0.022 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 145 MPa | 21000 psi | ISO 2039-1 |
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527 |
| Elongation at Break | 14 % | 14 % | ISO 527 |
| Tensile Modulus | 3.10 GPa | 450 ksi | ISO 527 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | DIN 53453 |
| NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.420 J/cm² | 2.00 ft-lb/in² | DIN 53453 |
| 0.380 J/cm² @Temperature -40.0 °C |
1.81 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Diofan® A602 Polyvinylidene Chloride (PVDC) (discontinued **)
- ICO Polymers ICORENEâ„¢ 195-1326 LMDPE Rotational Molding Resin
- Mitsubishi Hostaphan® RN, 30 micron Nominal Thickness Universal Polyethylene Terephthalate Film
- Karina E 85/227-D-AT-IS-SI PVC Compound
- ScanTube FEP Tubing
- A. Schulman POLYPUR™ FPU 1112 Thermoplastic Polyurethane Compound (15% Glass)
- Teknor Apex Telcar® TL-2683D Thermoplastic Elastomer
- A. Schulman CP814-01 Linear, Low-Density Polyethylene
- BASF Ultrason® E 2010 G4 MR SW 15102 20% Glass Filled PESU
- World Minerals Celite® Super Floss® Diatomaceous Earth Antiblock Additive
Copyright © lookpolymers.com All Rights Reserved