Multibase Multi-Pro® 4008 T Polypropylene

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	Multibase
Trade Name	Multi-Pro®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Multibase Multi-Pro® 4008 T Polypropylene.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Talc Filled, 40% by weight.Forms:PelletsProcessing Methods:Injection MoldingUses: ConnectorsElectrical/Electronic ApplicationsAppliancesInformation provided by Multibase

Physical Properties	Metric	English	Comments
Density	1.23 g/cc	0.0444 lb/in³	ASTM D792
Linear Mold Shrinkage	0.0090 cm/cm	0.0090 in/in	ASTM D955
Melt Flow	8.0 g/10 min	8.0 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	29.0 MPa	4200 psi	ASTM D638
Elongation at Break	30 %	30 %	ASTM D638
Flexural Modulus	3.10 GPa	450 ksi	ASTM D790
Izod Impact, Notched	0.427 J/cm	0.800 ft-lb/in	73°F; ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	116 °C	240 °F	Unannealed; ASTM D648

Processing Properties	Metric	English
Rear Barrel Temperature	199 - 221 °C	390 - 430 °F
Middle Barrel Temperature	204 - 232 °C	400 - 450 °F
Front Barrel Temperature	204 - 232 °C	400 - 450 °F
Nozzle Temperature	193 - 227 °C	380 - 440 °F
Mold Temperature	4.44 - 65.6 °C	40.0 - 150 °F
Drying Temperature	93.3 °C	200 °F
Dry Time	2 hour	2 hour
Back Pressure	0.138 - 0.345 MPa	20.0 - 50.0 psi
Screw Speed	40 - 100 rpm	40 - 100 rpm

Descriptive Properties	Value	Comments
Clamp Tonnage	2-4 tons/in²
Screw L/D Ratio	20:1