Multibase Multi-Pro® 2518 CU Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Multibase |
| Trade Name | Multi-Pro® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Pro® 2518 CU Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Calcium Carbonate Filler, 25% by weight.Features:Gloss, High Forms:PelletsProcessing Methods:Injection MoldingInformation provided by Multibase
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D955 |
| Melt Flow | 18 g/10 min | 18 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
| Elongation at Break | 150 % | 150 % | ASTM D638 |
| Flexural Modulus | 1.72 GPa | 250 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | 73°F; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 215 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 188 - 216 °C | 370 - 420 °F | |
| Middle Barrel Temperature | 199 - 232 °C | 390 - 450 °F | |
| Front Barrel Temperature | 199 - 232 °C | 390 - 450 °F | |
| Nozzle Temperature | 193 - 227 °C | 380 - 440 °F | |
| Mold Temperature | 4.44 - 65.6 °C | 40.0 - 150 °F | |
| Drying Temperature | 93.3 °C | 200 °F | |
| Dry Time | 2 hour | 2 hour | |
| Back Pressure | 0.138 - 0.345 MPa | 20.0 - 50.0 psi | |
| Screw Speed | 40 - 100 rpm | 40 - 100 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Clamp Tonnage | 2-4 tons/in2 | |
| Screw L/D Ratio | 20:1 |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-SEAL® 0862 Conductive Elastomer
- Arlon 920-410C##FR-P1 0.020" (0.508 mm) Cured Self-fusing Silicone Tape (discontinued **)
- LG Chemical Lupoy 1201HP-08 Polycarbonate Resin
- SABIC Innovative Plastics LNP LUBRICOMP OCP36F PPS - Linear
- Solvay Specialty Polymers KetaSpire® KT-880FP Polyetheretherketone (PEEK)
- SABIC Innovative Plastics LNP THERMOCOMP RC004SXS PA 66
- Total Lumicene® MR30MC2 Metallocene Random Copolymer Polypropylene, Injection Molding
- DSM Akulon® Fuel Lock FL-LP PA6
- Bostik 6328 Low Viscosity, Long Open Time, Flexible EVA Glue Stick
Copyright © lookpolymers.com All Rights Reserved