Multibase Multi-Pro® 2516 CU Polypropylene

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	Multibase
Trade Name	Multi-Pro®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Multibase Multi-Pro® 2516 CU Polypropylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Calcium Carbonate Filler, 25% by weight.Features:Gloss, High UV Resistance, Good Forms:PelletsProcessing Methods:Injection MoldingUses:FurnitureLawn and Garden EquipmentInformation provided by Multibase

Physical Properties	Metric	English	Comments
Density	1.08 g/cc	0.0390 lb/in³	ASTM D792
Linear Mold Shrinkage	0.011 cm/cm	0.011 in/in	ASTM D955
Melt Flow	16.5 g/10 min	16.5 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	24.7 MPa	3580 psi	ASTM D638
Elongation at Break	150 %	150 %	ASTM D638
Flexural Modulus	1.65 GPa	240 ksi	ASTM D790
Izod Impact, Notched	0.507 J/cm	0.950 ft-lb/in	73°F; ASTM D256
Gardner Impact	8.587 J	6.333 ft-lb	ASTM D3029

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	62.8 °C	145 °F	Unannealed; ASTM D648

Processing Properties	Metric	English
Rear Barrel Temperature	188 - 216 °C	370 - 420 °F
Middle Barrel Temperature	199 - 232 °C	390 - 450 °F
Front Barrel Temperature	199 - 232 °C	390 - 450 °F
Nozzle Temperature	193 - 227 °C	380 - 440 °F
Mold Temperature	4.44 - 65.6 °C	40.0 - 150 °F
Drying Temperature	93.3 °C	200 °F
Dry Time	2 hour	2 hour
Back Pressure	0.138 - 0.345 MPa	20.0 - 50.0 psi
Screw Speed	40 - 100 rpm	40 - 100 rpm

Descriptive Properties	Value	Comments
Clamp Tonnage	2-4 tons/in²
Screw L/D Ratio	20:1