- MRC Polymers MAXTELâ„¢ 600T10-BK TPO, 10% Talc Filled
MRC Polymers MAXTELâ„¢ 600T10-BK TPO, 10% Talc Filled
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) |
| Manufacturer | MRC Polymers |
| Trade Name | MAXTEL™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | MRC Polymers MAXTELâ„¢ 600T10-BK TPO, 10% Talc Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
For automotive exterior applicationsExcellent process ability and dimensional stabilityCan be UV StabilizedInternal and external lubricants can be addedInformation provided by MRC Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.980 g/cc | 0.980 g/cc | ISO 1183 |
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 230 °C |
17 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 58 | 58 | 15sec dwell; ISO 868 |
| Tensile Strength, Yield | 16.0 MPa | 2320 psi | ISO 527 |
| Flexural Strength | 22.0 MPa | 3190 psi | ISO 178 |
| Flexural Modulus | 1.05 GPa | 152 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 47.0 kJ/m² | 22.4 ft-lb/in² | |
| Gardner Impact | 19.21 J | 14.17 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 55.0 °C @Thickness 3.17 mm |
131 °F @Thickness 0.125 in |
un-annealed; ISO 75 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 182 - 204 °C | 360 - 400 °F | |
| Middle Barrel Temperature | 193 - 216 °C | 380 - 420 °F | |
| Front Barrel Temperature | 204 - 227 °C | 400 - 440 °F | |
| Nozzle Temperature | 216 - 238 °C | 420 - 460 °F | |
| Melt Temperature | 221 - 243 °C | 430 - 470 °F | |
| Mold Temperature | 21.1 - 32.2 °C | 70.0 - 90.0 °F | |
| Drying Temperature | 48.9 - 65.6 °C | 120 - 150 °F | Usually not required |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Injection Pressure | 48.3 - 55.2 MPa | 7000 - 8000 psi | |
| Back Pressure | 0.000 - 1.03 MPa | 0.000 - 150 psi | |
| Cushion | 0.635 cm | 0.250 in |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Fill Rate | Slow to Moderate | |
| Screw Speed | Slow to Moderate |
Users viewing this material also viewed the following:
- Inno-Comp INNOPOL® CS 2-3302 TO BU Elastomer Modified, UV-Stabilized Polypropylene Block-Copolymer
- ITW Plexus Plexusâ„¢ MA300 Methacrylate Adhesive
- Michelman® Michem® Emulsion 79535 Nonionic polyethylene / polypropylene blend
- Plenco 1500 Polyester, Granular, Transfer Molded
- Westlake Epolene® N-11P Nonemulsifiable - Low Molecular Weight Polyethylene Polymer
- Hexcel® HexForce™ 6080 Fiber Glass Fabric
- ExxonMobil LLDPE LL 6101XR Wire & Cable Linear Low Density Polyethylene Resin (European Grade)
- BASF Neopolen® P 9435 0.05 g/cc Core density; Expanded Polypropylene (Europe)
- Aptek DI-STRATE 1500-1 Microwave/RF Foam Substrate
- SABIC Innovative Plastics LNP Stat-kon MDM40 PP
Copyright © lookpolymers.com All Rights Reserved