PolyOne Synprene® RT-3840MS Thermoplastic Elastomer - SBC (discontinued **)

Category	Polymer , Thermoplastic , Elastomer, TPE , Styrenic TPE
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Synprene® RT-3840MS Thermoplastic Elastomer - SBC (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description/Features:High Performance Thermoplastic ElastomerTransparentUV StabilizedApplications:Multi-PurposeMarket:Consumer GoodsProcessing Method:Injection MoldingPolyOne First ChoiceInformation provided by PolyOne Corporation.

Physical Properties	Metric	English	Comments
Specific Gravity	0.900 g/cc	0.900 g/cc	ASTM D792
	0.900 g/cc	0.900 g/cc	ASTM D792
Linear Mold Shrinkage	0.0135 cm/cm	0.0135 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	40	40	Instant; ASTM D2240
	40	40	Instant; ASTM D2240
Tensile Strength, Yield	4.83 MPa	700 psi	Method A (Dumbbell & Section), 20 in/min; ASTM D412
	4.83 MPa	700 psi	Method A (Dumbbell & Section), 20 in/min, Break; ASTM D412
	2.31 MPa @Strain 300 %	335 psi @Strain 300 %	Method A (Dumbbell & Section), 20 in/min; ASTM D412
	2.31 MPa @Strain 300 %	335 psi @Strain 300 %	Method A (Dumbbell & Section), 20 in/min; ASTM D412
Elongation at Break	700 %	700 %	Method A (Dumbbell & Section), 20 in/min; ASTM D412
	700 %	700 %	Method A (Dumbbell & Section), 20 in/min; ASTM D412
Rebound	57 %	57 %	Bayshore; ASTM D2632
	57 %	57 %	Bayshore; ASTM D2632
Tear Strength	20.2 kN/m	115 pli	Die C (graves), 20 in/min; ASTM D624
	20.2 kN/m	115 pli	Die C (graves), 20 in/min; ASTM D624
Compression Set	20 %	20 %	Method B, 73°F(23°C), 22 hrs; ASTM D395
	20 %	20 %	Method B, 73°F(23°C), 22 hrs; ASTM D395

Thermal Properties	Metric	English	Comments
Brittleness Temperature	-65.0 °C	-85.0 °F	ASTM D746
	-65.0 °C	-85.0 °F	ASTM D746

Optical Properties	Metric	English	Comments
Transmission, Visible	90 %	90 %	transparent; thickness not quantified