MRC Polymers MAXTELâ„¢ 600 GF30 TPO, 30% Glass Fiber Filled
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) |
| Manufacturer | MRC Polymers |
| Trade Name | MAXTEL™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | MRC Polymers MAXTELâ„¢ 600 GF30 TPO, 30% Glass Fiber Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
For automotive exterior applicationsExcellent process ability and dimensional stabilityCan be UV StabilizedInternal and external lubricants can be addedInformation provided by MRC Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Filler Content | 30 % | 30 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D256 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 70 | 70 | 15sec dwell; ISO 868 |
| Tensile Strength at Break | 55.2 MPa | 8000 psi | ASTM D638 |
| Flexural Strength | 68.9 MPa | 10000 psi | ASTM D790 |
| Flexural Modulus | 3.79 GPa | 550 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm | 2.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C @Thickness 3.17 mm |
320 °F @Thickness 0.125 in |
un-annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 136 °C @Thickness 3.17 mm |
277 °F @Thickness 0.125 in |
un-annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 210 - 227 °C | 410 - 440 °F | |
| Middle Barrel Temperature | 210 - 227 °C | 410 - 440 °F | |
| Front Barrel Temperature | 210 - 227 °C | 410 - 440 °F | |
| Nozzle Temperature | 210 - 227 °C | 410 - 440 °F | |
| Melt Temperature | 221 - 260 °C | 430 - 500 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 4 hour | 4 hour | |
| Dew Point | <= -17.8 °C | <= 0.000 °F | |
| Drying Air Flow Rate | 22.7 - 28.3 l/min | 0.800 - 1.00 ft³/min (CFM) | per lb/hour resin processed |
| Injection Pressure | 68.9 - 138 MPa | 10000 - 20000 psi | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Cushion | 0.330 - 0.635 cm | 0.130 - 0.250 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Fill Rate | Slow to Moderate | |
| Hold Pressure | 40-60% of injection pressure | |
| Packing Pressure | 50-75% of injection pressure |
Users viewing this material also viewed the following:
- PolyOne Bergamid™ B65 G30 black IG Polyamide 6 (Nylon 6)
- Mateck Calcium Fluoride (CaF2)
- Teknor Apex APEX® 3210-60 Polyvinyl Chloride, Flexible
- Skamol Group SKAMOCAST 14-105 Insulating Castable
- Wieland Auropal W-2 Solder
- Chengdu Polyster H4543 Thermoplastic Polyether-ester Elastomer (TPEE)
- Diamond Polymers ABS 3502ELG
- 3M 7620-T Cold Shrink Silicone Rubber Termination Kits QT-III
- 3M QI-10/37-270 Cold Shrink Quick Insulator
- Arkema Group LOTRYL® 17 BA 04 Copolymer Ethylene - Butyl Acrylate
Copyright © lookpolymers.com All Rights Reserved