Toyobo PELPRENE™ P150B Polyester TPE
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | Toyobo |
| Trade Name | Pelprene™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo PELPRENE™ P150B Polyester TPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Polyester TPEInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.36 % | 0.36 % | 23°C, 65% RH |
| Linear Mold Shrinkage | 0.013 cm/cm @Thickness 2.00 mm |
0.013 in/in @Thickness 0.0787 in |
|
| Melt Index of Compound | 20 g/10 min @Temperature 230 °C |
20 g/10 min @Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 98 | 98 | JIS K6301 |
| Hardness, Shore D | 57 | 57 | ASTM D2240 |
| Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM D638 |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| 50% Modulus | 0.0196 GPa | 2.84 ksi | ASTM D638 |
| Flexural Modulus | 0.289 GPa | 41.9 ksi | ASTM D790 |
| Compressive Modulus | 0.0191 GPa | 2.77 ksi | 0.1; ASTM D695 |
| Resilience | 59 | 59 | JIS K6301 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Tear Strength | 177 kN/m | 1010 pli | ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 10 | 10 | ASTM D1044 |
| Compression Set | 60 % | 60 % | JIS K6301 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 140 µm/m-°C @Temperature 20.0 °C |
77.8 µin/in-°F @Temperature 68.0 °F |
TMA |
| Melting Point | 212 °C | 414 °F | By DSC |
| Maximum Service Temperature, Air | 117 °C | 243 °F | Heat deflection temperature, load unknown; ASTM D648 |
| Vicat Softening Point | 190 °C | 374 °F | ASTM D1525 |
| Brittleness Temperature | <= -65.0 °C | <= -85.0 °F | JIS K6301 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+14 ohm-cm | 2.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | JIS K2111 |
Users viewing this material also viewed the following:
- Kazanorgsintez PE2NT 11-9 High Density Polyethylene Composite
- KYDEX® 5555 MB Low Heat Release Aviation Thermoforming Sheet with Microban® Antimicrobial
- Formosa Plastics Formolene® 2610A Compounding and Injection Molding Polypropylene
- A. Schulman POLYBATCH™ Yellow 2200 Concentrate Based In Polyethylene
- Eastman Eastar MN004 Copolyester
- Diamond Polymers PC 2109T Natural, UV Stabilized, Flame Retardant Polycarbonate
- Carmel Olefins CAPILENE® E 50 E Polypropylene Homopolymer
- Asahi Kasei Thermylene® P6-20FG-0693 20% Glass Fiber Reinforced, Heat and UV Stabilized
- BASF Lucalen® A 2710 H Ethylene/Acrylate Copolymer
Copyright © lookpolymers.com All Rights Reserved