Lehmann & Voss LUVOCOM® 1700-1401 PPO, with carbon fiber and glass fiber
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1700-1401 PPO, with carbon fiber and glass fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts; low thermal coefficient of expansion.Electrically conductive, suitable for continuous discharging of statically generated electricity.High dimensionally stable precision parts with low warpage and narrow tolerance range.Control disks, cams, sliding elements and other duty parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ISO 1183 |
| Water Absorption | <= 0.060 % | <= 0.060 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | |
| Melt Flow | 15 g/10 min @Load 5.00 kg, Temperature 300 °C |
15 g/10 min @Load 11.0 lb, Temperature 572 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 100 MPa | 14500 psi | |
| Elongation at Yield | 1.5 % | 1.5 % | |
| 2.0 % | 2.0 % | flexural | |
| Modulus of Elasticity | 7.50 GPa | 1090 ksi | |
| Flexural Strength | 125 MPa | 18100 psi | |
| Flexural Modulus | 8.00 GPa | 1160 ksi | |
| Charpy Impact Unnotched | 1.80 J/cm² | 8.57 ft-lb/in² | flatwise; ISO 179 1fU |
| 1.60 J/cm² @Temperature -30.0 °C |
7.61 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179 1eA |
| 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 179 eA | |
| Coefficient of Friction, Dynamic | 0.22 | 0.22 | |
| Coefficient of Friction, Static | 0.20 | 0.20 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 50.0 µm/m-°C | 27.8 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 110 °C | 230 °F | |
| Vicat Softening Point | 145 °C | 293 °F | DIN ISO 306 |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1000 ohm | <= 1000 ohm | |
| Insulation Resistance | <= 10000 ohm | <= 10000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 280 °C | 536 °F | mass temp |
| Nozzle Temperature | 285 - 295 °C | 545 - 563 °F | |
| Zone 1 | 270 - 280 °C | 518 - 536 °F | |
| Zone 2 | 270 - 300 °C | 518 - 572 °F | |
| Zone 3 | 290 - 305 °C | 554 - 581 °F | |
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | |
| Drying Temperature | 95.0 - 110 °C @Time <=7200 sec |
203 - 230 °F @Time <=2.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 1510 CNU White Polypropylene
- DuPont Performance Polymers Crastin® SK608 BK509 PBT (Unverified Data**)
- Saint-Gobain Norton® T-200 Mechanical Grade PTFE Sheet (0.015" thick)
- A. Schulman PP 1255-01 Polypropylene General Purpose Homopolymer Polypropylene
- Universal Wire Works 901 (AMS 5660) Nickel Alloy Filler Metal
- Westlake Plastics Absylux® CN-F Acrylonitrile-Butadiene-Styrene (conductive)
- Master Bond EP30DP Abrasion Resistant Cryogenic Epoxy Urethane System
- BASF DiethylenetriaminE
- SABIC Innovative Plastics Lexan® EXL9414T PC Copolymer (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved