Lehmann & Voss LUVOCOM® 3-8269 Polyamide 6, with basalt fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Mineral Reinforced, Impact Grade |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 3-8269 Polyamide 6, with basalt fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, apparatus- and precision engineering.Strong, stiff parts; impact resistance.dynamic stressReduced moment of inertia compared with metal parts.Bearings, sleeves, control disks, gear wheels, cams.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 140 MPa | 20300 psi | |
| Elongation at Yield | 2.8 % | 2.8 % | |
| 3.6 % | 3.6 % | flexural | |
| Modulus of Elasticity | 10.0 GPa | 1450 ksi | |
| Flexural Strength | 205 MPa | 29700 psi | |
| Flexural Modulus | 9.00 GPa | 1310 ksi | |
| Charpy Impact Unnotched | 5.40 J/cm² | 25.7 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | |
| 210 °C | 410 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 270 °C | 518 °F | mass temp |
| Nozzle Temperature | 270 - 280 °C | 518 - 536 °F | |
| Zone 1 | 250 - 270 °C | 482 - 518 °F | |
| Zone 2 | 270 - 290 °C | 518 - 554 °F | |
| Zone 3 | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |
| Drying Temperature | 75.0 °C @Time 36000 - 57600 sec |
167 °F @Time 10.0 - 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 21600 sec |
221 °F @Time 4.00 - 6.00 hour |
or |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Nyco NYAD® 1250 Wollastonite
- Outokumpu 4016 Ferritic Stainless Steel
- Techmer ES HiFill® PEEK CF30 HF 30% Carbon Filled
- Teknor Apex Sinpolene CPP1050 Polypropylene
- A. Schulman POLYBATCH™ U-0294-L Blowing Agent Concentrate Based In PE
- Esstech V-117-1140 Barium Borosilicate Glass
- Dow Corning EL-8051 IN Silicone Organic Elastomer Blend
- American Computer Optics Medium-High Transmission Filter 6 mm
- Asahi Kasei Thermylene® P6-30FG-0709 30% Fiber Glass Reinforced, Heat Stabilized
- A. Schulman ComAlloy Hiloy® 756 Carbon Fiber Reinforced, Flow Enhanced, PPS Alloy
Copyright © lookpolymers.com All Rights Reserved