PolyOne Lubri-Tech™ MP-20CF/15T Modified Polyphenylene Oxide (mPPO), Carbon Fiber Reinforced, PTFE Lubricated
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ MP-20CF/15T Modified Polyphenylene Oxide (mPPO), Carbon Fiber Reinforced, PTFE Lubricated
.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Carbon Fiber ReinforcedPTFE LubricatedUL 94 HBPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ASTM D792 |
| Water Absorption | 0.014 % | 0.014 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 100 MPa | 14500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 2.41 GPa | 350 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Modulus | 10.3 GPa | 1500 ksi | ASTM D790 |
| Izod Impact, Notched | 0.854 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.60 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 146 °C | 295 °F | Annealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | Annealed, 0.125 in bars; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 100 - 10000 ohm-cm | 100 - 10000 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 293 - 327 °C | 560 - 620 °F | Molding |
| Mold Temperature | 93.3 - 121 °C | 200 - 250 °F | |
| Drying Temperature | 93.3 °C | 200 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- NIZHNEKAMSKNEFTEKHIM PE 4318Q (18403) Linear Low Density Polyethylene
- Honeywell Capran® Emblem™ 2530 Bi-Axially Oriented Nylon Film (discontinued **)
- Materion Beryllium Copper Alloy 25 Tube; HT (TH04) Temper; over 9.5 to 25.4 mm o.d. (UNS C17200)
- Lucite International Diakon® CLH952 Acrylic Polymer
- Solvay Specialty Polymers Algoflon® F 5 Polytetrafluoroethylene (PTFE)
- CeramTec Alunit® Aluminum Nitride
- DSM Stanyl® TE341 Nylon 46 (European Grade) (Dry)
- ACC MM230 Addition Cure 2-Part Molding Rubber
- Amity Thermosets ATG 115 Phenolic Molding Organic Filler, Compression Molded
- BASF Ultrason E 3010 PES
Copyright © lookpolymers.com All Rights Reserved