Lehmann & Voss LUVOCOM® 1502-7865/BK2 PPSU, unreinforced
| Category | Polymer , Thermoplastic , Polyphenylsulfone (PPSU) |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1502-7865/BK2 PPSU, unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistanceHigh chemical resistance parts.Inherent flame resistance.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ISO 1183 |
| Water Absorption | <= 0.50 % | <= 0.50 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | |
| Melt Flow | 45 g/10 min @Load 10.0 kg, Temperature 380 °C |
45 g/10 min @Load 22.0 lb, Temperature 716 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 75.0 MPa | 10900 psi | |
| Elongation at Yield | 8.0 % | 8.0 % | |
| 11 % | 11 % | flexural | |
| Modulus of Elasticity | 2.50 GPa | 363 ksi | |
| Flexural Strength | 110 MPa | 16000 psi | |
| Flexural Modulus | 2.00 GPa | 290 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 55.0 µm/m-°C | 30.6 µin/in-°F | DIN 53752 |
| Maximum Service Temperature, Air | 160 °C | 320 °F | |
| 180 °C | 356 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |
| Mold Temperature | 150 - 170 °C | 302 - 338 °F | |
| Drying Temperature | 140 °C @Time 14400 - 18000 sec |
284 °F @Time 4.00 - 5.00 hour |
or |
| 180 °C @Time 7200 - 10800 sec |
356 °F @Time 2.00 - 3.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | jet black |
Users viewing this material also viewed the following:
- Polykemi AB SCANMID 6 B12^ F40 Nylon 6, Glass Fiber Reinforced
- Kinlead PT12 Adhesive Tape Grade BOPP Plain Film (thickness: 28 µm)
- Indium Corp. Indalloy® 205 In-Pb Solder Alloy
- Lubriplate 630-A Lithium Based Multi-Purpose Grease
- Solvay Specialty Polymers Galden® D02TS PFPE Fluid
- SMAC SMACWRAP® EX Damping Material, 0.12 mm
- DSM Stanyl® TE351 PA46 FR(17)
- Covestro Makrolon® 1260 Polycarbonate, Impact Grade
- Covestro Texin® 985 Urethane Thermoplastic Elastomer
- 3M Cushion-Mount™ 1920M Plus Plate Mounting Tape
Copyright © lookpolymers.com All Rights Reserved