SABIC Innovative Plastics Xenoy® XL1562 PBT+PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® XL1562 PBT+PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
XENOY XL1562 is an impact modified PBT+PC blend with outstanding chemical resistance, good UV stability and flow properties.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.50 % @Temperature 23.0 °C |
0.50 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.011 cm/cm | 0.0080 - 0.011 in/in | on tensile bar; SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.011 cm/cm | 0.0080 - 0.011 in/in | on tensile bar; SABIC Method |
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 27 g/10 min @Load 5.00 kg, Temperature 250 °C |
27 g/10 min @Load 11.0 lb, Temperature 482 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 100 MPa | 14500 psi | ISO 2039-1 |
| Tensile Strength at Break | 42.0 MPa | 6090 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 100 % | 100 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.10 GPa | 305 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 74.0 MPa | 10700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.00 GPa | 290 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² @Temperature -30.0 °C |
8.57 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| 45.0 kJ/m² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 2.00 J/cm² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Taber Abrasion, mg/1000 Cycles | 30 @Load 1.00 kg |
30 @Load 2.20 lb |
CS-17; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 110 µm/m-°C @Temperature 23.0 - 80.0 °C |
61.1 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 110 µm/m-°C @Temperature 23.0 - 80.0 °C |
61.1 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.180 W/m-K | 1.25 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 125 °C | 257 °F | Rate B/50; ISO 306 |
| 128 °C | 262 °F | Rate B/120; ISO 306 | |
| 190 °C | 374 °F | Rate A/50; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
2nd value; UL 94 | |
| Glow Wire Test | 750 °C @Thickness 3.20 mm |
1380 °F @Thickness 0.126 in |
Glow Wire Flammability Index; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 2.8 @Frequency 50.0 - 60.0 Hz |
2.8 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Dielectric Strength | 17.0 kV/mm @Thickness 3.20 mm |
432 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| 25.0 kV/mm @Thickness 1.60 mm |
635 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | |
| 32.0 kV/mm @Thickness 0.800 mm |
813 kV/in @Thickness 0.0315 in |
in oil; IEC 60243-1 | |
| Dissipation Factor | 0.0020 @Frequency 50.0 - 60.0 Hz |
0.0020 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Kazanorgsintez E-13 Petroleum Resin
- Solvay Specialty Polymers Galden® D02 PFPE Fluid
- Spartech SP-9030 Economy ABS Sheet
- Techmer ES HiFill® TPX-HTN-01040 A 45% Glass Filled
- Bhansali Engineering Abstron SE-20P ABS Sheet Extrusion Grade
- Arkema Group Lacovyl® S 110 P PVC
- CIMBAR BARIMITE™ G-50 High Purity Barite (BaSO4)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 4.0 PHR MBT
- H.C. Starck Amperit® 551.059 Tungsten Carbide - Chromium Carbide - Nickel 70-20-7 (W-CrC-Ni)
- Techmer ES HiFill® ABS GF15 A1 15% Glass Filled
Copyright © lookpolymers.com All Rights Reserved