Lehmann & Voss LUVOCOM® 1-7390 Polyamide 66, with carbon fiber, PTFE, lubricant modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Carbon Fiber/PTFE Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1-7390 Polyamide 66, with carbon fiber, PTFE, lubricant modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Reduced moment of inertia compared with metal parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.High dimensionally stable precision parts with low warpage and narrow tolerance range.Gear parts for automotive appliances, control disks, cams, sliding elements.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 195 MPa | 28300 psi | |
| Elongation at Yield | 2.0 % | 2.0 % | |
| 2.5 % | 2.5 % | flexural | |
| Modulus of Elasticity | 21.0 GPa | 3050 ksi | |
| Flexural Strength | 260 MPa | 37700 psi | |
| Flexural Modulus | 17.0 GPa | 2470 ksi | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | flatwise; ISO 179 1fU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | |
| 150 °C | 302 °F | short term | |
| Flammability, UL94 | HB | HB | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1000 ohm | <= 1000 ohm | |
| Insulation Resistance | <= 1000 ohm | <= 1000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 290 °C | 554 °F | mass temp |
| Nozzle Temperature | 280 - 300 °C | 536 - 572 °F | |
| Zone 1 | 290 - 310 °C | 554 - 590 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 290 - 310 °C | 554 - 590 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 21600 - 57600 sec |
167 °F @Time 6.00 - 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 21600 sec |
221 °F @Time 4.00 - 6.00 hour |
Vacuum Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Gharda Chemicals G-PAEK™ 1200FCM Ultra High Performance PEK Polymer (discontinued **)
- Karina E 854-35/1-Y-ERYB Ivory PVC Compound
- A. Schulman POLYBATCH™ House Red 50311U/4 Concentrate Based In LLDPE
- Master Bond Mastersil 713 Low Viscosity One Component Silicone
- A. Schulman POLYAXIS® LP624 Stabilized High Density Polyethylene
- Covestro Makrolon® T 7435 Polycarbonate, High Impact
- DuPont Teijin Films Mylar® RL32 Polyester Packaging Film, 150 Gauge
- Arkema Group Rilsan® ASR 20 Nylon 12, 20% Carbon Fiber Filled (Conditioned)
- BASF Diisopropanolamine 90% Solution
- Beijing Chemical Industry KAIFA® M104 MPPO Resin
Copyright © lookpolymers.com All Rights Reserved