Lanxess Pocan® C 1202 000000 PET + PC

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer Lanxess
Trade Name Pocan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Pocan® C 1202 000000 PET + PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT + PC, non-reinforced, injection molding, improved impact strength, low tendency to warp, UV-stabilizedInformation provided by LANXESS.
Physical Properties Metric English Comments
Specific Gravity 1.21 g/cc
1.21 g/cc
ISO 1183
Bulk Density 0.800 g/cc
0.0289 lb/in³
ISO 60
Linear Mold Shrinkage, Flow 0.010 cm/cm
0.010 in/in
60x60x2; 250°C / WZ 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
60x60x2; 250°C / WZ 80°C; 600 bar; ISO 294-4
Melt Flow 45 g/10 min

@Load 5.00 kg,
Temperature 270 °C
 45 g/10 min

@Load 11.0 lb,
Temperature 518 °F
 ISO 1133-1
Mechanical Properties Metric English Comments
Tensile Strength, Yield 50.0 MPa
7250 psi
ISO 527-1, -2; 50 mm/min
Elongation at Break 10 %
10 %
ISO 527-1, -2; 50 mm/min
Elongation at Yield 4.0 %
4.0 %
ISO 527-1, -2; 50 mm/min
Tensile Modulus 2.10 GPa
305 ksi
ISO 527-1, -2; 1 mm/min
Flexural Strength 75.0 MPa

@Strain 5.50 %
 10900 psi

@Strain 5.50 %
 2 mm/min; ISO 178-A
Flexural Yield Strength 70.0 MPa

@Strain 3.50 %
 10200 psi

@Strain 3.50 %
 2 mm/min; ISO 178-A
Flexural Modulus 2.10 GPa
305 ksi
2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) 17.0 kJ/m²

@Temperature -30.0 °C
 8.09 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1A
50.0 kJ/m²

@Temperature 23.0 °C
 23.8 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ISO 180-1U
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 ISO 180-1U
Charpy Impact Unnotched NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ISO 179-1eU
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 ISO 179-1eU
Charpy Impact, Notched 1.80 J/cm²

@Temperature -30.0 °C
 8.57 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eA
5.50 J/cm²

@Temperature 23.0 °C
 26.2 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 50.0 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
CTE, linear, Transverse to Flow 90.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 50.0 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi) 100 °C
212 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
ISO 75-1, -2
Vicat Softening Point 120 °C

@Load 5.10 kg
 248 °F

@Load 11.2 lb
 120°C/hour; ISO 306
Processing Properties Metric English Comments
Melt Temperature 250 °C
482 °F
for test specimens; ISO 294
250 - 265 °C
482 - 509 °F
Mold Temperature 70.0 °C
158 °F
for test specimens; ISO 294
60.0 - 90.0 °C
140 - 194 °F
Drying Temperature 120 °C
248 °F
Dry Time 4 - 8 hour
4 - 8 hour
Moisture Content 0.00 - 0.020 %
0.00 - 0.020 %
residual; Karl Fischer Test
Descriptive Properties Value Comments
ISO Shortname ISO 7792-1-PBT+PC, GHLMPR, 11-020