- FKuR Kunststoff Biograde® C 9550 Biodegradable Plastic Compound
FKuR Kunststoff Biograde® C 9550 Biodegradable Plastic Compound
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Wood and Natural Products |
| Manufacturer | FKuR Kunststoff GmbH |
| Trade Name | Biograde® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | FKuR Kunststoff Biograde® C 9550 Biodegradable Plastic Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
BIOGRADE® are easy to process blends based on cellulose. BIOGRADE® is composed mainly of natural resources. Based on cellulose, a product of the paper industry BIOGRADE® has been especially designed for injection molding applications. BIOGRADE® is mainly composed of natural resource materials (European Soft Wood from sustainable forestry) and does not contain starch or starch derivatives.Information Provided by FKuR Kunststoff GmbH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.970 g/cc | 0.0350 lb/in³ | ISO 60 |
| Density | 1.67 g/cc | 0.0603 lb/in³ | ISO 1183 |
| Melt Flow | 5.0 - 9.0 g/10 min @Load 5.00 kg, Temperature 230 °C |
5.0 - 9.0 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 46.0 MPa | 6670 psi | ISO 527 |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | ISO 527 |
| Elongation at Break | 6.0 % | 6.0 % | ISO 527 |
| Elongation at Yield | 6.0 % | 6.0 % | ISO 527 |
| Tensile Modulus | 4.40 GPa | 638 ksi | ISO 527 |
| Flexural Yield Strength | 72.0 MPa | 10400 psi | at 3.5% strain; 6.5% strain at break; ISO 178 |
| Flexural Modulus | 4.95 GPa | 718 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.00 J/cm² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1/1eU |
| Charpy Impact, Notched | 0.300 J/cm² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | >= 180 °C | >= 356 °F | ISO 3146-C |
| Vicat Softening Point | 115 °C | 239 °F | A; ISO 306 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Melt Volume Flow (cm3/10 min) | 3-6 | ISO 1133; 230°C, 5kg |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Extrusion 87771 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Objet FullCure® 840 Vero Blue Resin for Rapid Prototyping
- Inno-Comp INNOPOL® CS 2-3302 TO BU Elastomer Modified, UV-Stabilized Polypropylene Block-Copolymer
- Lubriplate Brick Grease Specialty Lubricant and Grease
- ITW Plexus Plexusâ„¢ MA420FS Methacrylate Adhesive
- SABIC Innovative Plastics LNP Stat-kon NX03602 PC+ABS
- SABIC Innovative Plastics LNP STAT-KON SC004 PA 12 (Europe-Africa-Middle East)
- A. Schulman SCHULAMID® 6 GF33 33% Glass Fiber Reinforced Nylon 6
- Dow Corning Z-1227 METHYLVINYLDICHLOROSILANE
Copyright © lookpolymers.com All Rights Reserved