Lanxess Durethan® DP AKV 30 FN00 DUS013 Nylon 66, 30% Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® DP AKV 30 FN00 DUS013 Nylon 66, 30% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 66, 30% glass fibers, injection molding, halogen free flame retardantInformation provided by LANXESS.
Physical Properties Metric English Comments
Specific Gravity 1.43 g/cc
1.43 g/cc
ISO 1183
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0020 cm/cm
0.0020 in/in
60x60x2; 270°C / WZ 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0010 cm/cm
0.0010 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0070 cm/cm
0.0070 in/in
60x60x2; 270°C / WZ 80°C; 600 bar; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.0 MPa
10900 psi
cond.; ISO 527-1, -2; 5 mm/min
120 MPa
17400 psi
d.a.m.; ISO 527-1, -2; 5 mm/min
Elongation at Break 2.5 %
2.5 %
d.a.m.; ISO 527-1, -2; 5 mm/min
5.1 %
5.1 %
cond.; ISO 527-1, -2; 5 mm/min
Tensile Modulus 6.50 GPa
943 ksi
cond.; ISO 527-1, -2; 1 mm/min
10.5 GPa
1520 ksi
d.a.m.; ISO 527-1, -2; 1 mm/min
Flexural Strength 120 MPa

@Strain 4.80 %
 17400 psi

@Strain 4.80 %
 cond., 2 mm/min; ISO 178-A
190 MPa

@Strain 2.70 %
 27600 psi

@Strain 2.70 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Yield Strength 120 MPa

@Strain 3.50 %
 17400 psi

@Strain 3.50 %
 cond., 2 mm/min; ISO 178-A
Flexural Modulus 5.60 GPa
812 ksi
cond., 2 mm/min; ISO 178-A
9.30 GPa
1350 ksi
d.a.m., 2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
d.a.m.; ISO 180-1A
Izod Impact, Unnotched (ISO) 45.0 kJ/m²
21.4 ft-lb/in²
d.a.m.; ISO 180-1U
47.0 kJ/m²
22.4 ft-lb/in²
cond.; ISO 180-1U
Thermal Properties Metric English Comments
Melting Point 260 °C
500 °F
10°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi) >= 250 °C
>= 482 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 224 °C
435 °F
ISO 75-1, -2
Vicat Softening Point 240 °C

@Load 5.10 kg
 464 °F

@Load 11.2 lb
 120°C/hour; ISO 306
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
V-0

@Thickness 0.400 mm
 V-0

@Thickness 0.0157 in
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
Glow Wire Test 725 °C

@Diameter 0.850 mm
 1340 °F

@Diameter 0.0335 in
 GWIT; IEC 60695-2-13
725 °C

@Diameter 1.50 mm
 1340 °F

@Diameter 0.0591 in
 GWIT; IEC 60695-2-13
725 °C

@Diameter 3.00 mm
 1340 °F

@Diameter 0.118 in
 GWIT; IEC 60695-2-13
960 °C

@Diameter 0.800 mm
 1760 °F

@Diameter 0.0315 in
 GWFI; IEC 60695-2-12
960 °C

@Diameter 1.50 mm
 1760 °F

@Diameter 0.0591 in
 GWFI; IEC 60695-2-12
960 °C

@Diameter 3.00 mm
 1760 °F

@Diameter 0.118 in
 GWFI; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 5.00e+12 ohm-cm
5.00e+12 ohm-cm
cond.; IEC 60093
5.00e+15 ohm-cm
5.00e+15 ohm-cm
d.a.m.; IEC 60093
Surface Resistance 4.00e+14 ohm
4.00e+14 ohm
cond.; IEC 60093
3.00e+16 ohm
3.00e+16 ohm
d.a.m.; IEC 60093
Dielectric Constant 3.7

@Frequency 1.00e+6 Hz
 3.7

@Frequency 1.00e+6 Hz
 d.a.m.; IEC 60250
3.9

@Frequency 100 Hz
 3.9

@Frequency 100 Hz
 d.a.m.; IEC 60250
4.1

@Frequency 1.00e+6 Hz
 4.1

@Frequency 1.00e+6 Hz
 cond.; IEC 60250
8.7

@Frequency 100 Hz
 8.7

@Frequency 100 Hz
 cond.; IEC 60250
Dielectric Strength 34.8 kV/mm

@Thickness 1.00 mm
 884 kV/in

@Thickness 0.0394 in
 cond.; IEC 60243-1
38.5 kV/mm

@Thickness 1.00 mm
 978 kV/in

@Thickness 0.0394 in
 d.a.m.; IEC 60243-1
Dissipation Factor 0.0080

@Frequency 100 Hz
 0.0080

@Frequency 100 Hz
 d.a.m.; IEC 60250
0.012

@Frequency 1.00e+6 Hz
 0.012

@Frequency 1.00e+6 Hz
 d.a.m.; IEC 60250
0.070

@Frequency 1.00e+6 Hz
 0.070

@Frequency 1.00e+6 Hz
 cond.; IEC 60250
0.13

@Frequency 100 Hz
 0.13

@Frequency 100 Hz
 cond.; IEC 60250
Comparative Tracking Index 600 V
600 V
d.a.m.; Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 270 °C
518 °F
for test specimens; ISO 294
265 - 285 °C
509 - 545 °F
Mold Temperature 80.0 °C
176 °F
for test specimens; ISO 294
80.0 - 100 °C
176 - 212 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 2 - 6 hour
2 - 6 hour
Moisture Content 0.030 - 0.070 %
0.030 - 0.070 %
residual; Karl Fischer Test