- Lanxess Durethan® A 30 S FN31 000000 Nylon 66, Flame Retardant
Lanxess Durethan® A 30 S FN31 000000 Nylon 66, Flame Retardant
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® A 30 S FN31 000000 Nylon 66, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66, non-reinforced, injection molding, halogen-free flame retardant, improved flowabilityInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.169 g/cc | 1.169 g/cc | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.011 cm/cm | 0.011 in/in | 60x60x2; 270°C / WZ 80°C; 600 bar; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm | 0.0010 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.011 cm/cm | 0.011 in/in | 60x60x2; 270°C / WZ 80°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | cond.; ISO 527-1, -2; 50 mm/min |
| 85.0 MPa | 12300 psi | d.a.m.; ISO 527-1, -2; 50 mm/min | |
| Elongation at Yield | 4.1 % | 4.1 % | d.a.m.; ISO 527-1, -2 |
| >= 20 % | >= 20 % | cond.; ISO 527-1, -2 | |
| Tensile Modulus | 1.50 GPa | 218 ksi | cond.; ISO 527-1, -2; 1 mm/min |
| 3.80 GPa | 551 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min | |
| Flexural Strength | 55.0 MPa @Strain 7.80 % |
7980 psi @Strain 7.80 % |
cond., 2 mm/min; ISO 178-A |
| 125 MPa @Strain 5.80 % |
18100 psi @Strain 5.80 % |
d.a.m., 2 mm/min; ISO 178-A | |
| Flexural Yield Strength | 40.0 MPa @Strain 3.50 % |
5800 psi @Strain 3.50 % |
cond., 2 mm/min; ISO 178-A |
| 120 MPa @Strain 3.50 % |
17400 psi @Strain 3.50 % |
d.a.m., 2 mm/min; ISO 178-A | |
| Flexural Modulus | 1.60 GPa | 232 ksi | cond., 2 mm/min; ISO 178-A |
| 3.70 GPa | 537 ksi | d.a.m., 2 mm/min; ISO 178-A | |
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² | <= 4.76 ft-lb/in² | d.a.m.; ISO 180-1A |
| <= 10.0 kJ/m² | <= 4.76 ft-lb/in² | cond.; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 55.0 kJ/m² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 180-1U |
| 55.0 kJ/m² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 180-1U | |
| 60.0 kJ/m² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 180-1U | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
cond.; ISO 180-1U | |
| Charpy Impact Unnotched | 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 179-1eU |
| 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 179-1eU | |
| 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 179-1eU | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
cond.; ISO 179-1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² | <= 4.76 ft-lb/in² | d.a.m.; ISO 179-1eA |
| <= 1.00 J/cm² | <= 4.76 ft-lb/in² | cond.; ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| Melting Point | 265 °C | 509 °F | 10°C/min; ISO 11357-1, -3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75-1, -2 |
| Vicat Softening Point | 230 °C @Load 5.10 kg |
446 °F @Load 11.2 lb |
120°C/hour; ISO 306 |
| Flammability, UL94 | V-0 @Thickness 0.400 mm |
V-0 @Thickness 0.0157 in |
|
| Oxygen Index | 34 % | 34 % | Method A; ISO 4589-2 |
| Glow Wire Test | 775 °C @Diameter 0.400 mm |
1430 °F @Diameter 0.0157 in |
GWIT; IEC 60695-2-13 |
| 960 °C @Diameter 0.400 mm |
1760 °F @Diameter 0.0157 in |
GWFI; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | cond.; IEC 60093 |
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | d.a.m.; IEC 60093 | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | cond.; IEC 60093 |
| 1.00e+15 ohm | 1.00e+15 ohm | d.a.m.; IEC 60093 | |
| Dielectric Constant | 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
d.a.m.; IEC 60250 |
| 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
d.a.m.; IEC 60250 | |
| 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
cond.; IEC 60250 | |
| 8.0 @Frequency 100 Hz |
8.0 @Frequency 100 Hz |
cond.; IEC 60250 | |
| Dielectric Strength | 25.0 kV/mm @Thickness 1.00 mm |
635 kV/in @Thickness 0.0394 in |
cond.; IEC 60243-1 |
| 30.0 kV/mm @Thickness 1.00 mm |
762 kV/in @Thickness 0.0394 in |
d.a.m.; IEC 60243-1 | |
| Dissipation Factor | 0.012 @Frequency 100 Hz |
0.012 @Frequency 100 Hz |
d.a.m.; IEC 60250 |
| 0.019 @Frequency 1.00e+6 Hz |
0.019 @Frequency 1.00e+6 Hz |
d.a.m.; IEC 60250 | |
| 0.055 @Frequency 1.00e+6 Hz |
0.055 @Frequency 1.00e+6 Hz |
cond.; IEC 60250 | |
| 0.20 @Frequency 100 Hz |
0.20 @Frequency 100 Hz |
cond.; IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | d.a.m.; Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | for test specimens; ISO 294 |
| 260 - 270 °C | 500 - 518 °F | ||
| Mold Temperature | 80.0 °C | 176 °F | for test specimens; ISO 294 |
| 80.0 - 100 °C | 176 - 212 °F | ||
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.030 - 0.070 % | 0.030 - 0.070 % | residual; Karl Fischer Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO1874-PA 66, GFHR, 12-040; ISO 1043 PA FR(30) |
Users viewing this material also viewed the following:
- Kazanorgsintez Diproxamine 157-65M
- Gouda Vuurvast VIBRON 130 Dense Vibrating Refractory Castable
- Lubriplate L0804 Non-Detergent Motor Oil Motor Oil & Transmission Fluid
- Momentive Performance Materials Siloprenâ„¢ LSR 2010 Liquid Silicone Rubber - General Purpose
- Karina E 80/200-D-IS Clear PVC Compound
- SABIC Innovative Plastics NORYL WCD861A PPE-TPE (Europe-Africa-Middle East)
- SABIC Innovative Plastics PC2200 PC (Europe-Africa-Middle East)
- A. Schulman POLYBATCH™ White LL8575 AP Concentrate Based In LLDPE
- 3M Scotchlite™ 680-81 Reflective Graphic Film
Copyright © lookpolymers.com All Rights Reserved