LG Chemical XG568 MABS, Anti-Scratch, High Gloss

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer LG Chemical
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical XG568 MABS, Anti-Scratch, High Gloss.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Injection Molding, Anti-Scratch, High GlossApplication: LCD TV Front Cabinet, Bezel, Audio/Video HousingCSA No. 9011-14-7 and 9003-56-9Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.11 g/cc
1.11 g/cc
ASTM D792
Water Absorption 0.30 %

@Temperature 23.0 °C,
Time 86400 sec
 0.30 %

@Temperature 73.4 °F,
Time 24.0 hour
 ASTM D570
Maximum Moisture Content 0.010
0.010
Injection Molding
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm

@Thickness 3.20 mm
 0.0020 - 0.0040 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 19.5 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 19.5 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 114
114
ASTM D785
Tensile Strength, Yield 53.0 MPa

@Thickness 3.20 mm
 7680 psi

@Thickness 0.126 in
 50 mm/min; ASTM D638
Elongation at Break 20 %

@Thickness 3.20 mm
 20 %

@Thickness 0.126 in
 50 mm/min; ASTM D638
Elongation at Yield >= 6.0 %

@Thickness 3.20 mm
 >= 6.0 %

@Thickness 0.126 in
 50 mm/min; ASTM D638
Flexural Yield Strength 85.3 MPa

@Thickness 3.20 mm
 12400 psi

@Thickness 0.126 in
 15 mm/min; ASTM D790
Flexural Modulus 2.75 GPa

@Thickness 3.20 mm
 398 ksi

@Thickness 0.126 in
 15 mm/min; ASTM D790
Izod Impact, Notched 0.883 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 1.65 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D256
0.883 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 1.65 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Izod Impact, Unnotched 0.392 J/cm

@Thickness 6.40 mm,
Temperature -20.0 °C
 0.735 ft-lb/in

@Thickness 0.252 in,
Temperature -4.00 °F
 ASTM D256
0.392 J/cm

@Thickness 3.20 mm,
Temperature -20.0 °C
 0.735 ft-lb/in

@Thickness 0.126 in,
Temperature -4.00 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 86.0 °C

@Thickness 3.20 mm
 187 °F

@Thickness 0.126 in
 ASTM D648
88.0 °C

@Thickness 6.40 mm
 190 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 82.0 °C

@Thickness 3.20 mm
 180 °F

@Thickness 0.126 in
 ASTM D648
83.0 °C

@Thickness 6.40 mm
 181 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Flammability, UL94 HB

@Thickness >=1.60 mm
 HB

@Thickness >=0.0630 in
HB

@Thickness >=3.20 mm
 HB

@Thickness >=0.126 in
Processing Properties Metric English Comments
Rear Barrel Temperature 180 - 200 °C
356 - 392 °F
Injection Molding
Middle Barrel Temperature 190 - 210 °C
374 - 410 °F
Injection Molding
Front Barrel Temperature 200 - 220 °C
392 - 428 °F
Injection Molding
Nozzle Temperature 200 - 220 °C
392 - 428 °F
Injection Molding
Melt Temperature 200 - 230 °C
392 - 446 °F
Injection Molding
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Injection Molding
Drying Temperature 80.0 - 90.0 °C
176 - 194 °F
Injection Molding
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Injection Molding
Back Pressure 29.4 - 58.8 MPa
4260 - 8530 psi
Injection Molding
Screw Speed 30 - 60 rpm
30 - 60 rpm
Injection Molding
Descriptive Properties Value Comments
Ozone Resistance No Crack
5 sec, JIS K6301