LG Chemical Lupox® HV1005S PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | LG Chemical |
| Trade Name | Lupox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical Lupox® HV1005S PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PBT, High ImpactApplication: IT/OA, Automotive (Connector)CAS No. 155123-66-3 and 24968-12-5Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.012 - 0.020 cm/cm @Thickness 3.20 mm |
0.012 - 0.020 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa @Thickness 3.20 mm |
7250 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | >= 100 % @Thickness 3.20 mm |
>= 100 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 73.5 MPa @Thickness 3.20 mm |
10700 psi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Flexural Modulus | 2.06 GPa @Thickness 3.20 mm |
299 ksi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 0.441 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
0.827 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | @ Break; ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C @Thickness 6.40 mm |
129 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 230 - 235 °C | 446 - 455 °F | Injection Molding |
| Middle Barrel Temperature | 235 - 245 °C | 455 - 473 °F | Injection Molding |
| Front Barrel Temperature | 235 - 245 °C | 455 - 473 °F | Injection Molding |
| Nozzle Temperature | 240 - 250 °C | 464 - 482 °F | Injection Molding |
| Melt Temperature | 240 - 250 °C | 464 - 482 °F | Injection Molding |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Injection Molding |
| Drying Temperature | 100 - 120 °C | 212 - 248 °F | Injection Molding |
| Dry Time | 3.00 - 5.00 hour | 3.00 - 5.00 hour | Injection Molding |
Users viewing this material also viewed the following:
- PolyOne Trilliant™ HC THC-02 1200 IL Natural Polyamide 66 (Nylon 66)
- Nye Lubricants 759P (NG) Synthetic Oil
- LyondellBasell Adsylâ„¢ 5 C 30 F Polyolefin
- Sumitomo Bakelite North America RX® 3-1-501N-P Mineral Filled Diallyl Phthalate
- DSM Akulon® S223-D (Dry) Nylon 66 (North America)
- Colorite Polymers CS8039UL Wire and Cable Insulation Vinyl Compound
- Eurotec® Tecotek® PC30 NL TD 700 PC, unfilled, flame retardant - halogen (RoHS compliant), impact modified, natural
- 3M FP0861 Removable Clear Polypropylene Label Products
- 3M Scotchkote™ HG 519 Epoxy Ceramic HD Surfacer
- BCC Products BC 6005 Epoxy Surface Coat
Copyright © lookpolymers.com All Rights Reserved