LATI Latigloss 57 G/40 F2 PPA, 40% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 40% Glass Fiber Reinforced
Manufacturer LATI
Trade Name Latigloss
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latigloss 57 G/40 F2 PPA, 40% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product with high mechanical properties and exceptional surface finish based on Semi-aromatic polyamide (PPA). Glass fibers. Potentially suitable for food/medical contact applicationAvailability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.53 g/cc
0.0553 lb/in³
Linear Mold Shrinkage, Flow 0.0025 - 0.0045 cm/cm
0.0025 - 0.0045 in/in
Linear Mold Shrinkage, Transverse 0.0045 - 0.0070 cm/cm
0.0045 - 0.0070 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 65.0 MPa

@Temperature 150 °C
 9430 psi

@Temperature 302 °F
125 MPa

@Temperature 120 °C
 18100 psi

@Temperature 248 °F
175 MPa

@Temperature 90.0 °C
 25400 psi

@Temperature 194 °F
195 MPa

@Temperature 60.0 °C
 28300 psi

@Temperature 140 °F
210 MPa

@Temperature 23.0 °C
 30500 psi

@Temperature 73.4 °F
Elongation at Break 1.9 %

@Temperature 23.0 °C
 1.9 %

@Temperature 73.4 °F
2.1 %

@Temperature 60.0 °C
 2.1 %

@Temperature 140 °F
2.3 %

@Temperature 90.0 °C
 2.3 %

@Temperature 194 °F
4.0 %

@Temperature 120 °C
 4.0 %

@Temperature 248 °F
8.0 %

@Temperature 150 °C
 8.0 %

@Temperature 302 °F
Tensile Modulus 4.00 GPa

@Temperature 150 °C
 580 ksi

@Temperature 302 °F
9.00 GPa

@Temperature 120 °C
 1310 ksi

@Temperature 248 °F
11.5 GPa

@Temperature 90.0 °C
 1670 ksi

@Temperature 194 °F
13.0 GPa

@Temperature 60.0 °C
 1890 ksi

@Temperature 140 °F
14.5 GPa

@Temperature 23.0 °C
 2100 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 6.00 J/cm²
28.6 ft-lb/in²
Charpy Impact, Notched 0.850 J/cm²
4.04 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 145 °C
293 °F
Deflection Temperature at 0.46 MPa (66 psi) 290 °C
554 °F
Deflection Temperature at 1.8 MPa (264 psi) 265 °C
509 °F
Vicat Softening Point 260 °C

@Load 5.00 kg
 500 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 310 - 340 °C
590 - 644 °F
Mold Temperature 150 - 170 °C
302 - 338 °F
Drying Temperature 120 - 130 °C

@Time 10800 sec
 248 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa